Adsorbents | Gas component | References |
O2 | N2 |
|
Extended Langmuir |
LiX | k1 = 7.87 × 10−9 mol/kg/Pa k2 = 1541.211 K k3 = 6.79 × 10−10 1/Pa k4 = 1968.24 K | k1 = 9.86 × 10−9 mol/kg/Pa k2 = 2010.908 K k3 = 1.67 × 10−10 1/Pa k4 = 2250 K | Yang et al. [36] |
Li94.5Na1.5-X | k1 = 1.14 × 10−6 mol/kg k2 = 239.2 K k3 = 2.20 × 10−3 1/atm k4 = 1092 K | k1 = 1.69 × 10−6 mol/kg k2 = 134.4 K k3 = 1.19 × 10−3 1/atm k4 = 1990 K | Hutson et al. [37] |
Li94.2Na0.7Ag1.1-X | k1 = 0.965 × 10−6 mol/kg k2 = 196 K k3 = 2.25 × 10−3 1/atm k4 = 1212 K | k1 = 2.12 × 10−6 mol/kg k2 = 64.82 K k3 = 7.78 × 10−3 1/atm k4 = 1494 K |
|
Extended Langmuir–Freundlich |
13X | k1 = 6.705 × 10−3 mol/g k2 = −1.435 × 10−5 mol/g/K k3 = 3.253 × 10−4 1/atm k4 = 1428 K k5 = −0.3169 k6 = 387.8 K | k1 = 12.52 × 10−3 mol/g k2 = −1.785 × 10−5 mol/g/K k3 = 2.154 × 10−4 1/atm k4 = 2333 K k5 = 1.666 k6 = −245.2 K | Jee et al. [38] |
5A | k1 = 7.252 × 10−3 mol/g k2 = −1.820 × 10−5 mol/g/K k3 = 54.19 × 10−4 1/atm k4 = 662.6 K k5 = −1.101 k6 = 656.4 K | k1 = 6.21 × 10−3 mol/g k2 = −1.27 × 10−5 mol/g/K k3 = 1.986 × 10−4 1/atm k4 = 1970 K k5 = 2.266 k6 = −396.5 K | Jee et al. [39] |
Li-LSX | k1 = 0.4789 × 10−3 mol/g k2 = 636.6 K k3 = 94.8 × 10−4 1/atm k4 = 500 K k5 = 1.08168 | k1 = 1.84559 × 10−3 mol/g k2 = 139.68 K k3 = 2.19 × 10−4 1/atm k4 = 2484.2 K k5 = 1.033 | Epiepang et al. [40] |
Ca-LSX | k1 = 0.01448 × 10−3 mol/g k2 = 1385.97 K k3 = 1278.8 × 10−4 1/atm k4 = 207.35 K k5 = 1.152 | k1 = 0.2623 × 10−3 mol/g k2 = 646.75 K k3 = 0.688 × 10−4 1/atm k4 = 3785.11 K k5 = 0.931 |
Li2.5Ca46.75-LSX | k1 = 1.89933 × 10−3 mol/g k2 = 145.55 K k3 = 6.20294 × 10−4 1/atm k4 = 1609.13 K k5 = 1.021 | k1 = 1.31846 × 10−3 mol/g k2 = 104.23 K k3 = 0.19726 × 10−4 1/atm k4 = 3489.63 K k5 = 0.958 |
Li4.2Ca45.9-LSX | k1 = 2.20255 × 10−3 mol/g k2 = 179.35 K k3 = 4.02105 × 10−4 1/atm k4 = 1525.38 K k5 = 0.992 | k1 = 0.98863 × 10−3 mol/g k2 = 149.34 K k3 = 0.467445 × 10−4 1/atm k4 = 3243.35 K k5 = 0.999 |
|