Experimental Study on Seismic Fatigue Capacity of High- and Mild-Strength Structural Steels with and without Corrosion
Table 7
Cyclic fatigue test data of S355 steel made of 10 mm thick sheet.
| Yield stress: 390 MPa | Ultimate stress: 542 MPa | Sample number | Sample diameter (mm) | Stress applied (MPa) | The number of cycles | Average number of cycles | Sample status at the end of the cycle |
| 1 | 5.96 | 400 | 50895 | 50858 | Failure | 2 | 5.95 | 50432 | 3 | 5.99 | 51247 |
| 4 | 5.65 | 395 | 268396 | 255831 | Failure | 5 | 5.96 | 248659 | 6 | 5.99 | 250439 |
| 7 | 6.01 | 390 | 178459 | 182441 | Failure | 8 | 6.03 | 181432 | 9 | 5.92 | 187432 |
| 10 | 5.93 | 380 | 375242 | 361173 | Failure | 11 | 5.91 | 367529 | 12 | 5.92 | 340750 |
| 13 | 5.64 | 370 | 567476 | 554080 | Failure | 14 | 5.96 | 554375 | 15 | 5.96 | 540389 |
| 16 | 5.63 | 360 | 970450 | 964576 | Failure | 17 | 5.95 | 964389 | 18 | 5.96 | 958888 |
| 19 | 5.91 | 350 | 1259487 | 1265098 | Failure | 20 | 5.95 | 1260348 | 21 | 5.63 | 1275459 |
| 22 | 5.84 | 340 | 1659432 | 1715909 | Failure | 23 | 5.98 | 1740400 | 24 | 5.99 | 1747896 |
| 25 | 5.95 | 320 | 2059456 | 2013440 | Failure | 26 | 6.01 | 1979869 | 27 | 6.02 | 2000997 |
| 28 | 5.95 | 300 | 2687512 | 2654319 | Failure | 29 | 5.94 | 2679436 | 30 | 5.91 | 2596010 |
| 31 | 5.95 | 260 | 3459658 | 3443070 | Failure | 32 | 5.98 | 3654895 | 33 | 5.99 | 3214658 |
| 34 | 5.95 | 250 | 7524136 | 5757359 | Failure | 35 | 5.63 | 4500403 | 36 | 5.98 | 5247540 |
| 37 | 5.91 | 245 | 11095900 | 11298364 | No failure | 38 | 5.99 | 12694108 | 39 | 6.01 | 10105084 |
| 40 | 5.96 | 240 | 11454300 | 11455100 | No failure | 41 | 5.95 | 11564200 | 42 | 5.99 | 11346800 |
| 43 | 5.96 | 200 | 12897989 | 12890890 | No failure | 44 | 5.95 | 12984698 | 45 | 5.98 | 12789985 |
|
|