Experimental Study on Seismic Fatigue Capacity of High- and Mild-Strength Structural Steels with and without Corrosion
Table 6
Cyclic fatigue test data of S235 steel made of 10 mm thick sheet.
| Yield stress: 260 MPa | Ultimate stress: 372 MPa | Sample number | Sample diameter (mm) | Stress applied (MPa) | The number of cycles | Average number of cycles | Sample status at the end of the cycle |
| 1 | 5.95 | 250 | 268830 | 371057 | Failure | 2 | 5.92 | 404627 | 3 | 6.01 | 439715 |
| 4 | 5.94 | 240 | 595450 | 628358 | Failure | 5 | 5.91 | 630297 | 6 | 5.94 | 659327 |
| 7 | 5.95 | 230 | 827124 | 812358 | Failure | 8 | 6.02 | 807659 | 9 | 6.01 | 802400 |
| 10 | 5.95 | 220 | 1114521 | 1140315 | Failure | 11 | 5.95 | 1120896 | 12 | 5.95 | 1185527 |
| 13 | 5.64 | 210 | 1214591 | 1267647 | Failure | 14 | 5.96 | 1228941 | 15 | 5.96 | 1359410 |
| 16 | 6.01 | 200 | 1444297 | 1464158 | Failure | 17 | 6.02 | 1450677 | 18 | 5.94 | 1497500 |
| 19 | 5.99 | 190 | 1510297 | 1537064 | Failure | 20 | 5.95 | 1551497 | 21 | 5.96 | 1549400 |
| 22 | 5.94 | 180 | 1554200 | 1699594 | Failure | 23 | 5.99 | 1775123 | 24 | 6.01 | 1769459 |
| 25 | 6.02 | 170 | 3701311 | 3642997 | Failure | 26 | 5.91 | 3549479 | 27 | 5.96 | 3678200 |
| 28 | 5.93 | 160 | 6197897 | 6517851 | Failure | 29 | 5.95 | 6596359 | 30 | 5.98 | 6759297 |
| 31 | 5.95 | 150 | 10452400 | 10480652 | No failure | 32 | 5.63 | 10387259 | 33 | 5.98 | 10602297 |
| 34 | 5.91 | 145 | 11256759 | 11608130 | No failure | 35 | 5.99 | 11452327 | 36 | 6.01 | 12115304 |
|
|