Facile Solution Route to Synthesize Nanostructure Li4Ti5O12 for High Rate Li-Ion Battery

Tran, M. V.; Huynh, N. L. T.; Nguyen, T. T.; Ha, D. T. C.; Le, P. M. L.

doi:https://doi.org/10.1155/2016/4261069

Journal of Nanomaterials

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Special Issue

Functional Nanomaterials for Renewable Energy and Sustainability

View this Special Issue

Research Article | Open Access

Volume 2016 | Article ID 4261069 | https://doi.org/10.1155/2016/4261069

Facile Solution Route to Synthesize Nanostructure Li₄Ti₅O₁₂ for High Rate Li-Ion Battery

M. V. Tran,¹N. L. T. Huynh,²T. T. Nguyen,³D. T. C. Ha,¹and P. M. L. Le^1,2

Academic Editor: Zheng Zhang

Received28 Sept 2016

Accepted21 Nov 2016

Published25 Dec 2016

Abstract

High rate Li-ion batteries have been given great attention during the last decade as a power source for hybrid electric vehicles (HEVs, EVs, etc.) due to the highest energy and power density. These lithium batteries required a new design of material structure as well as innovative electrode materials. Among the promising candidates, spinel Li₄Ti₅O₁₂ has been proposed as a high rate anode to replace graphite anode because of high capacity and a negligible structure change during intercalation of lithium. In this work, we synthesized a spinel Li₄Ti₅O₁₂ in nanosize by a solution route using LiOH and Ti(OBu)₄ as precursor. An evaluation of structure and morphology by XRD and SEM exhibited pure spinel phase Li₄Ti₅O₁₂ and homogenous nanoparticles around 100 nm. In the charge-discharge test, nanospinel Li₄Ti₅O₁₂ presents excellent discharge capacity 160 mAh/g at rate C/10, as well as good specific capacities of 120, 110, and 100 mAh/g at high rates C, 5C and 10C, respectively.

1. Introduction

Since the first investigation of lithium’s intercalation by Colbow et al. in 1989 [1], spinel Li₄Ti₅O₁₂ has become one of attractive anode materials for Li-ion battery application because of nontoxic, inexpensive, thermal stability and negligible changed volume cell during charge-discharge cycling with a specific capacity of approximately 175 mAh/g [2, 3]. The process of reversible intercalation occurs around 1.55 V (versus Li⁺/Li), which is higher than its of lithiated graphite (below 1 V) to avoid the formation of unstable solid electrolyte interface (SEI) [1, 4, 5]. Despite these advantages, the inconveniences still exist in spinel phase Li₄Ti₅O₁₂ such as a low electronic conductivity and a poor lithium diffusion rate which limited its application in high rate Li-ion batteries [6, 7]. To overcome these problems, nanoscale particles size or 1D–3D nanostructure of Li₄Ti₅O₁₂ (nanowires, nanosheets, nanoparticles, nanotubes, nanorods, and microspheres) has been proposed to improve the electrochemical performances (higher specific capacity, high rate capability, and good charge-discharge cycling stability) due to shortening the diffusion way of lithium [8–14]. Table 1 summarized the highlighted results of Li₄Ti₅O₁₂ reported in the literature.

The remarkable results are mostly reported for using hydrothermal synthesis pathway with strictly controlled parameters such as temperature and pressure. However, these conditions are quite difficult for large scale application in the industry.

In this work, we report a facile solution way to synthesize nanospinel Li₄Ti₅O₁₂ through the formation of intermediate C-base centered orthorhombic Li_1.81H_0.19Ti₂O₅·2H₂O (LTH). The presence of LTH seems to be easily converted in Li₄Ti₅O₁₂ phase at low temperature range (<700°C) compared to the same layered structure α/β-Li₂TiO₃, usually obtained in solid state reaction or hydrothermal process [15]. Nanospinel Li₄Ti₅O₁₂ synthesized is investigated by charge-discharge test at high rate 1C to 10C. The diffusion coefficient of lithium ions () in the host Li₄Ti₅O₁₂ can be also determined by cyclic voltammetry.

2. Experimental

For the preparation of nanostructured Li₄Ti₅O₁₂, 7 mL solution of Ti(OBu)₄ ( = 1.491 g/mL at 20°C, = 340,39 g/mole) was added dropwise into 25 mL solution of LiOH 1 M solution under vigorous stirring at 4–6°C and the ratio of Li : Ti was 1 : 1.33. The low temperature is required to keep the hydrolyze process of Ti(OBu)₄ occurring slowly for limitation of TiO₂ rutile. Thus, the expected intermediate is certainly pure without emerging TiO₂ rutile, the as-prepared powder was collected through a centrifuge and washed many times with deionized water to neutral pH. The as-prepared powders were aged in the air by two steps: at 100°C for 36 hours to form C-base centered orthorhombic Li_1.81H_0.19Ti₂O₅·2H₂O (LTH). The intermediate phase was calcined at 600°C for 6 hours in the air to transfer to the spinel phase of Li₄Ti₅O₁₂.

The sample was identified by X-Ray Diffraction (XRD) performed with a D8-Advance (Bruker) diffractometer using CuKα radiation ( = 1.5408 Å). XRD pattern was collected in the range 10–70° (0.029°/s). Lattice parameters were calculated by software Celref. The Raman spectra were measured with a LaBRAM HR 800 (Jobin-Yvon-Horiba) Raman microspectrometer, using a He:Ne laser (632.8 nm) as the excitation source. The morphology and the distribution of grain size were determined by using Scanning Electron Microscope (FE-SEM S4800 Hitachi, Japan).

The electrode paste was prepared by mixing of Li₄Ti₅O₁₂ with acetylene black and polytetrafluoroethylene (PTFE) at a weight ratio of 80 : 15 : 5. The paste was laminated to 0.1 mm thickness, cut into pellets with a diameter of 10 mm, and dried at 130°C under a vacuum in 24 hours. The electrochemical properties of nanocrystalline Li₄Ti₅O₁₂ were evaluated by the cyclic voltammetry (CV) and the charge-discharge test at a various rate (from C/10 to 10C) in Swagelok cells. The cyclic voltammetry (CV) of nanospinel Li₄Ti₅O₁₂ has been performed in potential range of 1–2.5 V (versus Li⁺/Li) in the various rates from 10 μV/s to 100 μV/s. An electrode Li₄Ti₅O₁₂ and Li foil were used as the positive and negative materials in the half-cell and a solution of 1 M LiPF₆ in a mixture of ethylene carbonate (EC) and dimethyl carbonate (DMC) at a ratio of EC : DCM = 2 : 1 was used as the electrolyte.

3. Results and Discussion

3.1. Structure and Morphology

The formation of intermediate C-base centered orthorhombic Li_1.81H_0.19Ti₂O₅·2H₂O was determined by XRD patterns as shown in Figure 1. According to previous studies [1, 2, 12], structure of Li₄Ti₅O₁₂ is a cubic spinel (unit cell parameter around 8.36 Å) with space group of F3dm and can be represented as [Li₃][Li₁Ti₅][O₁₂]. Most of ions Li⁺ are situated at the tetrahedral 8a site, while the rest of ion Li⁺ and ions Ti⁴⁺ occupy randomly the octahedral 16d sites with a ratio of 1 : 5; and the oxygen atoms totally are located at the 32e site. As shown in Figure 2, the XRD patterns of sample could be identified to a pure phase of spinel Li₄Ti₅O₁₂ (JCPDS: 49-0207) [2, 13]. The broadening of diffraction peaks was related to the nanoparticles size. The lattice parameter of Li₄Ti₅O₁₂ was evaluated by seven diffraction peaks and calculated to be = 8.3564 Å (±0.0172 Å). This value was in good agreement with the published results [2, 14, 16–18].

Despite a heat treatment at 600°C in the last step, the peaks of XRD pattern were still quite large. It is considered that the sample was crystallized in small particle sizes. According to the Debye-Scherrer formula (1), the average size of particles was calculated from the full width of half maximum (FWHM) of diffraction peaks.where is the average size, is the constant depending on the crystallite shape (0.9), is the wavelength of copper Kα X-ray radiation (1.5406 Å), β is the FWHM of the most intense peak, and θ is the diffraction angle. The size reached around 40 nm. The nanosize of particles will suggest a fast kinetic of intercalation of lithium ion due to shortening the way diffusion [6, 7].

Following the theoretical calculation of A[B₂]O₄ spinel-type compound, spinel phase Li₄Ti₅O₁₂ consists of a symmetric group with the five expected , , Raman active vibration [19–22]. The Raman spectrum of nanostructure was shown in Figure 3 in the region of wave number between 150 and 900 cm⁻¹. In the high frequency, two modes at 671 cm⁻¹ and 740 cm⁻¹ (vibration mode ) were assigned to the vibrations of Ti–O bonds in [TiO₆] octahedra, while the stretching vibrations of the Li–O bonds in [LiO₄] and [LiO₆] polyhedra were characterized by two modes in region medium frequency 430 cm⁻¹ and 374 cm⁻¹, respectively. Two last modes in low frequency were attributed to the bending vibrations of O–Ti–O bonds (235 cm⁻¹) and O–Li–O bonds (160 cm⁻¹). These Raman spectra features were similar to those reported by Julien et al. [19].

The SEM and TEM images of nanostructure Li₄Ti₅O₁₂ in Figure 4 indicated particles shape mostly like a rod and its size fell into the nanometric scale around 100 nm. A good distribution and nanoparticle size were in good coherence with large XRD peaks.

(a)

(b)

3.2. Electrochemical Properties

The spinel phase Li₄Ti₅O₁₂ can insert/extract electrochemically 3 Li⁺ ions per mole reversibility in the potential 1.55 V (versus Li⁺/Li) causing the reduction of couple redox Ti⁴⁺/Ti³⁺ within a specific capacity theoretical of 175 mAh/g [1]. The process of intercalation of lithium ions seems to be a two-phase mechanism, similar to the olivine LiFePO₄ [23, 24]. All intercalating lithium ions inserted into the 16c octahedral site and the lithium ions initial in the tetrahedral 8a site moved simultaneously to the 16c octahedral site. Hence, the route diffusion of lithium ions into spinel Li₄Ti₅O₁₂ can be represented following the pathway 16c–8a–16c. The fully discharged compound can be described as [Li₆][LiTi₅][O₁₂] [25, 26]. In particular, the lithiation/delithiation of this spinel accompanies a “zero strain” characteristic; it means that lattice parameter of Li₄Ti₅O₁₂ remained constant between the initial state of Li₄Ti₅O₁₂ and the final state of Li₇Ti₅O₁₂ [2, 3, 14].

The electrochemical performance of nanospinel Li₄Ti₅O₁₂ synthesized has been investigated by cyclic voltammetry (CV) within 1–2.5 V (versus Li⁺/Li) and galvanostatic cycling within 1–2.5 V (versus Li⁺/Li). As shown in Figure 5(a), a symmetric couple redox peak was observed in 1.50 V (peak cathode) and 1.60 V (peak anode), corresponding to a reaction of couple redox Ti⁴⁺/Ti³⁺ at lowest rate 10 μV/s. A sharp form of two peaks characterized a two-phase mechanism of lithium insertion and related to a large plateau voltage (~1.55 V versus Li⁺/Li) in galvanostatic curves charge-discharge [24, 26]. Figure 5(a) also exhibited the evolution of CV curves of nanospinel Li₄Ti₅O₁₂ in the various rate from 10 μV/s to 100 μV/s. Following the increase of scan rate, it could be noticed that peak’s position shifted around 300 mV in highest rate 100 μV/s and the redox peaks broadened gradually. The diffusion coefficient of lithium ions () in the host Li₄Ti₅O₁₂ electrode can be determined from a linear relationship between peak currents () and the square root of the scan rate () from the CV curves, according to the following Randles-Sevcik equation (2) [27]:where is the peak current, is the surface area of electrode (0.785 cm²), is the number of electrons transfer per molecule (), is the concentration of lithium ion in Li₄Ti₅O₁₂ electrode, is scan rate, and is the diffusion coefficient of lithium ions.

(a)

(b)

It can be seen from Figure 5(b) in the plots of as a function of the square root of the scan rate () that a good linear relation between and was observed. The diffusion coefficient of lithium ions was found to be 3.8 × 10⁻¹² cm²/s, which was in accord with other authors’ results [6, 7].

Discharge-charge profiles of spinel Li₄Ti₅O₁₂ could be described by three regions: a quick drop of voltage corresponding to a region of solid solution with a content of lithium below 0.2, a main region of two-phase mechanism displayed by a plateau voltage in 1.55 V, and other solid solution region after plateau voltage [2, 14, 23]. The discharge-charge profiles in 1st cycle of nanospinel Li₄Ti₅O₁₂ at rate C/10, 1C, and 10C were shown in Figure 6(a). The curve in rate 1C seems to quasi-superimpose onto its rate C/10 without polarization, while huge polarization around 150 mV was observed in the curve in rate 10C. The polarization brought about shortening of plateau voltage in 1.4 V and decreased a content of lithium ion inserted. In the first cycle, nanospinel Li₄Ti₅O₁₂ could insert 3 Li⁺ ions at C/10, 2.6 at 1C, and 2.3 at 10C corresponding to a specific capacity of 175 mAh/g, 150 mAh/g, and 110 mAh/g, respectively [28]. Figures 6(b) and 6(c) presented the typical curves of discharge-charge at 1C and 10C. At the high rate, an excellent performance of nanospinel Li₄Ti₅O₁₂ was observed, in spite of the gradual decrease of lithium ion amount intercalated after some decade cycles. After 100 cycles (Figure 6(d)), the remaining capacities were 86% (rate C/10), 74% (rate 1C), and 75% (rate 10C) of capacity initial that were registered, corresponding to a specific capacity of 150 mAh/g, 111 mAh/g, and 100 mAh/g, respectively. We believe that the particles in nanosize shorten the pathway diffusion of lithium ions and encourage the performance of spinel Li₄Ti₅O₁₂ synthesized during the high rate capability test. These results are comparable with the previous studies which showed a specific capacity of 150 mAh/g in rate 1C and 100 mAh/g in rate 10C [9, 11, 15].

(a)

(b)

(c)

(d)

The rate capability of charge-discharge test from 1C to 10C was shown in Figure 7. Whatever the rate, a remarkable stability is obtained and the discharge-charge curves show clearly the effect of polarization to a decrease of specific capacity. The capacity obtained was 150 mAh/g at 1C, 130 mAh/g at 2C, 120 mAh/g at 5C, and 98 mAh/g at 10C. The specific capacity and cycling stability are comparably equal to these values obtained for 1D–3D nanostructure Li₄Ti₅O₁₂ synthesized by hydrothermal, solvothermal, electrospinning, and so forth [17, 18, 29, 30]. In the high rate performance, the electrode polarization was absolutely controlled by the limitation of internal resistance (ohmic drop), charge transfer, and mass transfer. Hence, the performance at high rate of nanospinel Li₄Ti₅O₁₂ would require an optimization of the electrode formation process, typically using a composite of spinel and high conductivities matrix carbon like CNTs or graphene [28, 31, 32].

(a)

(b)

4. Conclusions

This study has showed a facilitated route to synthesize nanospinel Li₄Ti₅O₁₂ through intermediate phase. The nanospinel had good distribution grains and the average of particles was around 100 nm. The diffusion coefficients of lithium ions determined from CV curves reached 3.8 × 10⁻¹² cm²/s. In a high rate of charge-discharge, an excellent electrochemical performance of nanospinel was observed and the specific capacities of 110 mAh/g and 100 mAh/g were achieved at 1C and 10C rate, respectively. The rate capability test showed a relation between a specific capacity and electrode polarization. Further studies regarding the role of CNTs or graphene could increase electronic conductivities electronic of electrode to improve the performance of this spinel phase.

Competing Interests

The authors declare that they have no competing interests.

Acknowledgments

This research is funded by Vietnam National University Ho Chi Minh City (VNU-HCM) under Grants HS2013-76-01 and TX2016-18-04. The authors would like to thank Office of Naval Research Global (ONRG) for Grant N62909-13-1-N235.

References

K. M. Colbow and R. R. Dahn Haering Jr., “Structure and electrochemistry of the spinel oxides LiTi₂O₄ and Li₄/₃Ti₅/₃O₄,” Journal of Power Sources, vol. 26, no. 3-4, pp. 397–402, 1989.
View at: Publisher Site | Google Scholar
T. Ohzuku, A. Ueda, and N. Yamamoto, “Zero-strain insertion material of Li[Li_1/3]Ti_5/3O₄ for rechargeable lithium cells,” Journal of the Electrochemical Society, vol. 142, no. 5, pp. 1431–1435, 1995.
View at: Publisher Site | Google Scholar
K. Ariyoshi, R. Yamato, and T. Ohzuku, “Zero-strain insertion mechanism of Li[ ${Li}_{1/3}$ ${Ti}_{5/3}$ ]O₄ for advanced lithium-ion (shuttlecock) batteries,” Electrochimica Acta, vol. 51, no. 6, pp. 1125–1129, 2005.
View at: Publisher Site | Google Scholar
D. Guerard and A. Herold, “Intercalation of lithium into graphite and other carbons,” Carbon, vol. 13, no. 4, pp. 337–345, 1975.
View at: Publisher Site | Google Scholar
Y. F. Reynier, R. Yazami, and B. Fultz, “Thermodynamics of lithium intercalation into graphites and disordered carbons,” Journal of the Electrochemical Society, vol. 151, no. 3, pp. A422–A426, 2004.
View at: Publisher Site | Google Scholar
T.-F. Yi, S.-Y. Yang, and Y. Xie, “Recent advances of Li₄Ti₅O₁₂ as a promising next generation anode material for high power lithium-ion batteries,” Journal of Materials Chemistry A, vol. 3, no. 11, pp. 5750–5777, 2015.
View at: Publisher Site | Google Scholar
B. Zhao, R. Ran, M. Liu, and Z. Shao, “A comprehensive review of Li₄Ti₅O₁₂-based electrodes for lithium-ion batteries: the latest advancements and future perspectives,” Materials Science and Engineering R: Reports, vol. 98, pp. 1–71, 2015.
View at: Publisher Site | Google Scholar
A. Guerfi, S. Sévigny, M. Lagacé, P. Hovington, K. Kinoshita, and K. Zaghib, “Nano-particle Li₄Ti₅O₁₂ spinel as electrode for electrochemical generators,” Journal of Power Sources, vol. 119–121, pp. 88–94, 2003.
View at: Publisher Site | Google Scholar
J. Kim and J. Cho, “Spinel Li₄Ti₅O₁₂ nanowires for high-rate li-ion intercalation electrode,” Electrochemical and Solid-State Letters, vol. 10, no. 3, pp. A81–A84, 2007.
View at: Publisher Site | Google Scholar
Y. Qiao, X. Hu, Y. Liu, and Y. Huang, “Li₄Ti₅O₁₂ nanocrystallites for high-rate lithium-ion batteries synthesized by a rapid microwave-assisted solid-state process,” Electrochimica Acta, vol. 63, pp. 118–123, 2012.
View at: Publisher Site | Google Scholar
H.-C. Chiu and G. P. Demopoulos, “A novel green approach to synthesis of nanostructured Li₄Ti₅O₁₂ anode material,” ECS Transactions, vol. 50, pp. 119–126, 2013.
View at: Google Scholar
E. Ferg, R. J. Gummow, A. de Kock, and M. M. Thackeray, “Spinel anodes for lithium-ion batteries,” Journal of the Electrochemical Society, vol. 141, no. 11, pp. L147–L150, 1994.
View at: Publisher Site | Google Scholar
D. Tsubone, T. Hashimoto, K. Igarashi, and T. Shimizu, “Electrical characterization of phase changes in lithium titanate,” Journal of the Ceramic Society of Japan, vol. 102, pp. 180–184, 1994.
View at: Google Scholar
S. Bach, J. P. Pereira-Ramos, and N. Baffler, “Electrochemical properties of sol-gel ${Li}_{4 /3}$ ${Ti}_{5/3}$ O₄,” Journal of Power Sources, vol. 81-82, pp. 273–276, 1999.
View at: Publisher Site | Google Scholar
I. Veljković, D. Poleti, L. J. Karanović, M. Zdujić, and G. Branković, “Solid state synthesis of extra phase-pure Li₄Ti₅O₁₂ spinel,” Science of Sintering, vol. 43, no. 3, pp. 343–351, 2011.
View at: Publisher Site | Google Scholar
A. Nugroho, S. J. Kim, K. Y. Chung, B.-W. Cho, Y.-W. Lee, and J. Kim, “Facile synthesis of nanosized Li₄Ti₅O₁₂ in supercritical water,” Electrochemistry Communications, vol. 13, no. 6, pp. 650–653, 2011.
View at: Publisher Site | Google Scholar
J. Lim, E. Choi, V. Mathew et al., “Enhanced high-rate performance of Li₄Ti₅O₁₂ nanoparticles for rechargeable Li-ion batteries,” Journal of the Electrochemical Society, vol. 158, no. 3, pp. A275–A280, 2011.
View at: Publisher Site | Google Scholar
S. C. Lee, S. M. Lee, J. W. Lee et al., “Spinel Li₄Ti₅O₁₂ nanotubes for energy storage materials,” Journal of Physical Chemistry C, vol. 113, no. 42, pp. 18420–18423, 2009.
View at: Publisher Site | Google Scholar
C. M. Julien, M. Massot, and K. Zaghib, “Structural studies of Li_4/3Me_5/3O₄ (Me = Ti, Mn) electrode materials: local structure and electrochemical aspects,” Journal of Power Sources, vol. 136, no. 2, pp. 72–79, 2004.
View at: Publisher Site | Google Scholar
I. A. Leonidov, O. N. Leonidova, L. A. Perelyaeva, R. F. Samigullina, S. A. Kovyazina, and M. V. Patrakeev, “Structure, ionic conduction, and phase transformations in lithium titanate Li₄Ti₅O₁₂,” Physics of the Solid State, vol. 45, no. 11, pp. 2183–2188, 2003.
View at: Publisher Site | Google Scholar
D. Z. Liu, W. Hayes, M. Kurmoo, M. Dalton, and C. Chen, “Raman scattering of the Li_1+xTi_2−xO4 superconducting system,” Physica C: Superconductivity, vol. 235-240, no. 2, pp. 1203–1204, 1994.
View at: Publisher Site | Google Scholar
R. Baddour-Hadjean and J.-P. Pereira-Ramos, “Raman microspectrometry applied to the study of electrode materials for lithium batteries,” Chemical Reviews, vol. 110, no. 3, pp. 1278–1319, 2010.
View at: Publisher Site | Google Scholar
D. Li and H. Zhou, “Two-phase transition of Li-intercalation compounds in Li-ion batteries,” Materials Today, vol. 17, no. 9, pp. 451–463, 2014.
View at: Publisher Site | Google Scholar
S. Scharner, W. Weppner, and P. Schmid-Beurmann, “Evidence of two‐phase formation upon lithium insertion into the Li_1.33Ti_1.67O₄ spinel,” Journal of the Electrochemical Society, vol. 146, no. 3, pp. 857–861, 1999.
View at: Publisher Site | Google Scholar
M. Vijayakumar, S. Kerisit, K. M. Rosso et al., “Lithium diffusion in Li₄Ti₅O₁₂ at high temperatures,” Journal of Power Sources, vol. 196, no. 4, pp. 2211–2220, 2011.
View at: Publisher Site | Google Scholar
D. V. Safronov, S. A. Novikova, A. M. Skundin, and A. B. Yaroslavtsev, “Lithium intercalation and deintercalation processes in Li₄Ti₅O₁₂ and LiFePO₄,” Inorganic Materials, vol. 48, no. 1, pp. 57–61, 2012.
View at: Publisher Site | Google Scholar
A. J. Bard and L. R. Faulkner, Electrochemical Methods and Applications, Wiley-Interscience, New York, NY, USA, 2000.
Y. Shi, L. Wen, F. Li, and H.-M. Cheng, “Nanosized Li₄Ti₅O₁₂/graphene hybrid materials with low polarization for high rate lithium ion batteries,” Journal of Power Sources, vol. 196, no. 20, pp. 8610–8617, 2011.
View at: Publisher Site | Google Scholar
Y. Li, G. L. Pan, J. W. Liu, and X. P. Gao, “Preparation of Li₄Ti₅O₁₂ nanorods as anode materials for lithium-ion batteries,” Journal of the Electrochemical Society, vol. 156, no. 7, pp. A495–A499, 2009.
View at: Publisher Site | Google Scholar
D. K. Lee, H.-W. Shim, J. S. An et al., “Synthesis of heterogeneous Li₄Ti₅O₁₂ nanostructured anodes with long-term cycle stability,” Nanoscale Research Letters, vol. 5, no. 10, pp. 1585–1589, 2010.
View at: Publisher Site | Google Scholar
N. Cao, L. Wen, Z. Song et al., “Li₄Ti₅O₁₂/reduced graphene oxide composite as a high-rate anode material for lithium ion batteries,” Electrochimica Acta, vol. 209, pp. 235–243, 2016.
View at: Publisher Site | Google Scholar
B. Li, F. Ning, Y.-B. He et al., “Synthesis and characterization of long life Li₄Ti₅O₁₂/C composite using amorphous TiO₂ nanoparticles,” International Journal of Electrochemical Science, vol. 6, pp. 3210–3223, 2011.
View at: Google Scholar

Copyright

Copyright © 2016 M. V. Tran et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1147

Downloads

1098

Citations