A Low-Cost Polytetrafluoroethylene-Framed TiO₂ Electrode Decorated with Oleic Acid-Capped CdSe Quantum Dots for Solar Cell

Table 1

Parameters obtained from photocurrent-voltage (𝐼-𝑉) measurement of the TiO₂/CdSe QD and TiO₂/MPA/CdSe QD QDSSC cells with different TiO₂ film thicknesses indicated in brackets.

Electrode	𝐼max (mA)	𝑉max (mV)	𝐼sc (mA)	𝑃max (mW)	𝐽sc (mA/cm^2)	𝑉oc (mV)	FF (%)	𝜂 (%)
TiO2 (25 µm)/MPA/CdSe QD	0.36	249.94	0.57	0.09	1.14	399.93	39.25	0.18
TiO2 (25 µm)/CdSe QD	0.32	199.94	0.49	0.06	0.98	349.91	36.90	0.13
TiO2 (30 µm)/MPA/CdSe QD	0.26	199.93	0.38	0.05	0.77	349.93	38.67	0.11
TiO2 (30 µm)/CdSe QD	0.27	149.91	0.39	0.04	0.80	249.96	40.60	0.08