Bond Behavior of Wet-Bonded Carbon Fiber-Reinforced Polymer-Concrete Interface Subjected to Moisture
Table 2
Test results of all specimens.
| Specimen ID | Exposure (month) | (MPa) | Average | (mm) | Average | (N⋅mm/mm2) | Average | (kN) | Average | Failure mode |
| RH-A-0-1 | 0 | 5.464 | 5.670 | 0.034 | 0.038 | 0.229 | 0.277 | 3.619 | 4.364 | AD | RH-A-0-2 | 5.875 | 0.041 | 0.348 | 4.508 | AD | RH-A-0-3 | 5.670 | 0.039 | 0.254 | 4.964 | AD | RH-A-1-1 | 1 | 7.422 | 6.021 | 0.057 | 0.043 | 0.625 | 0.406 | 5.255 | 4.786 | AD | RH-A-1-2 | 6.337 | 0.033 | 0.375 | 4.462 | AD | RH-A-1-3 | 4.304 | 0.038 | 0.219 | 4.641 | AD | RH-A-3-1 | 3 | 4.999 | 6.036 | 0.066 | 0.051 | 0.363 | 0.395 | 3.931 | 4.468 | AD | RH-A-3-2 | 7.475 | 0.048 | 0.493 | 4.657 | AD | RH-A-3-3 | 5.636 | 0.037 | 0.328 | 4.817 | AD | RH-A-6-1 | 6 | 4.640 | 5.103 | 0.045 | 0.038 | 0.262 | 0.274 | 3.639 | 4.023 | AD | RH-A-6-2 | 5.709 | 0.040 | 0.320 | 4.324 | AD | RH-A-6-3 | 4.960 | 0.027 | 0.240 | 4.105 | AD | RH-A-12-1 | 12 | 5.057 | 4.192 | 0.039 | 0.035 | 0.253 | 0.206 | 3.887 | 3.898 | AD | RH-A-12-2 | 3.315 | 0.036 | 0.164 | 4.311 | AD | RH-A-12-3 | 4.204 | 0.031 | 0.200 | 3.497 | AD | RH-B-0-1 | 0 | 5.521 | 5.685 | 0.039 | 0.042 | 0.252 | 0.287 | 3.820 | 4.179 | AD | RH-B-0-2 | 6.179 | 0.041 | 0.324 | 4.587 | AD | RH-B-0-3 | 5.355 | 0.044 | 0.285 | 4.130 | AD | RH-B-1-1 | 1 | 5.215 | 5.491 | 0.049 | 0.043 | 0.404 | 0.350 | 4.666 | 4.453 | AD | RH-B-1-2 | 5.649 | 0.038 | 0.336 | 4.111 | AD | RH-B-1-3 | 5.609 | 0.041 | 0.311 | 4.582 | AD | RH-B-3-1 | 3 | 6.144 | 6.249 | 0.039 | 0.040 | 0.397 | 0.376 | 4.734 | 4.667 | AD | RH-B-3-2 | 5.708 | 0.036 | 0.267 | 4.417 | AD | RH-B-3-3 | 6.894 | 0.044 | 0.463 | 4.850 | AD | RH-B-6-1 | 6 | 5.084 | 5.598 | 0.052 | 0.046 | 0.366 | 0.365 | 4.671 | 4.590 | AD | RH-B-6-2 | 4.913 | 0.035 | 0.286 | 4.451 | AD | RH-B-6-3 | 6.797 | 0.051 | 0.443 | 4.649 | AD | RH-B-12-1 | 12 | 3.560 | 4.519 | 0.036 | 0.037 | 0.224 | 0.243 | 4.127 | 4.134 | AD | RH-B-12-2 | 5.478 | 0.037 | 0.263 | 4.141 | AD | RH-B-12-3 | — | | — | — | AD | RH-C-0-1 | 0 | 7.819 | 8.842 | 0.048 | 0.050 | 0.499 | 0.572 | 5.307 | 5.662 | CO | RH-C-0-2 | 9.841 | 0.053 | 0.710 | 6.532 | CO | RH-C-0-3 | 8.865 | 0.050 | 0.507 | 5.146 | CO | RH-C-1-1 | 1 | 8.172 | 9.600 | 0.056 | 0.058 | 0.850 | 0.887 | 7.148 | 6.725 | CO | RH-C-1-2 | 10.495 | 0.056 | 0.864 | 6.562 | CO | RH-C-1-3 | 10.132 | 0.062 | 0.948 | 6.464 | CO | RH-C-3-1 | 3 | 8.067 | 7.163 | 0.057 | 0.063 | 0.517 | 0.554 | 5.345 | 5.747 | CO | RH-C-3-2 | 5.895 | 0.049 | 0.368 | 4.997 | C/A | RH-C-3-3 | 7.528 | 0.082 | 0.776 | 6.900 | CO | RH-C-6-1 | 6 | 5.868 | 7.492 | 0.051 | 0.064 | 0.563 | 0.611 | 5.941 | 6.212 | AD | RH-C-6-2 | 7.778 | 0.088 | 0.671 | 6.145 | C/A | RH-C-6-3 | 8.830 | 0.054 | 0.597 | 6.551 | C/A | RH-C-12-1 | 12 | 9.332 | 8.182 | 0.050 | 0.051 | 0.471 | 0.487 | 5.601 | 5.586 | AD | RH-C-12-2 | — | — | — | — | AD | RH-C-12-3 | 7.032 | 0.052 | 0.504 | 5.571 | AD |
|
|
Note. AD: adhesive failure; CO: cohesive failure; C/A: mixed cohesive/adhesive failure.
|