Insights into the Enhancement Mechanisms of Molten Salt Nanofluids
Table 4
Thermal conductivity and thermal diffusivity of base salt, SiO2-nfs, and MgO-nfs.
| Material | 525 °C | 550 °C | 600 °C | 650 °C | 700 °C |
| Base salt | α (mm2/s) | 0.207 | 0.212 | 0.230 | 0.223 | 0.217 | λ (W/(m·K)) | 0.641 | 0.651 | 0.700 | 0.671 | 0.644 | MgO-nfs | α (mm2/s) | 0.242 | 0.236 | 0.239 | 0.250 | 0.248 | λ (W/(m·K)) | 0.997 | 0.967 | 0.969 | 1.002 | 0.983 | Enhancement (%) | 55.7 | 48.6 | 38.4 | 49.3 | 52.5 | SiO2-nfs | α (mm2/s) | 0.218 | 0.215 | 0.243 | 0.230 | 0.234 | λ (W/(m·K)) | 0.807 | 0.793 | 0.885 | 0.830 | 0.835 | Enhancement (%) | 26.0 | 21.9 | 26.4 | 23.7 | 29.6 |
|
|