A Novel Coating of Orthodontic Archwires with Chlorhexidine Hexametaphosphate Nanoparticles
Table 2
Comparison of the CHX elusion (μmole) of coated SSW and NiTiW.
| Duration | Groups | N | Min | Max | Mean | SD | SE | Shapiro–Wilk test ( value) | Independent samples t-test ( value) |
| 1 day | SSW | 10 | 8.50 | 13.15 | 10.24 | 1.51 | 0.48 | 0.265 | 0.02 | NiTiW | 10 | 10.12 | 14.23 | 11.89 | 1.36 | 0.43 | 0.691 |
| 7 days | SSW | 10 | 16.86 | 21.10 | 18.49 | 1.32 | 0.41 | 0.425 | 0.001 | NiTiW | 10 | 17.97 | 23.58 | 21.20 | 1.83 | 0.57 | 0.529 |
| 14 days | SSW | 10 | 27.14 | 31.59 | 29.23 | 1.33 | 0.42 | 0.961 | 0.034 | NiTiW | 10 | 28.72 | 32.00 | 30.50 | 1.14 | 0.36 | 0.648 |
| 21 days | SSW | 10 | 33.89 | 37.43 | 36.00 | 1.12 | 0.35 | 0.623 | 0.471 | NiTiW | 10 | 33.50 | 37.00 | 35.60 | 1.26 | 0.40 | 0.328 |
| 28 days | SSW | 10 | 40.75 | 45.86 | 43.48 | 1.78 | 0.56 | 0.561 | 0.007 | NiTiW | 10 | 44.00 | 47.00 | 45.43 | 0.98 | 0.31 | 0.826 |
|
|
The mean difference is significant at the 0.05 level.
|