Effect of Sepiolite-Loaded Fe<sub>2</sub>O<sub>3</sub> on Flame Retardancy of Waterborne Polyurethane

Xu, Tong; Qian, Di; Hu, Yelei; Zhu, Yuanzhao; Zhong, Yi; Zhang, Linping; Xu, Hong; Peng, Huaxin; Mao, Zhiping

doi:https://doi.org/10.1155/2021/3596591

Advances in Polymer Technology

On this page

Abstract Introduction Experimental Discussion Conclusion Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2021 | Article ID 3596591 | https://doi.org/10.1155/2021/3596591

Effect of Sepiolite-Loaded Fe₂O₃ on Flame Retardancy of Waterborne Polyurethane

Tong Xu,¹Di Qian,¹Yelei Hu,¹Yuanzhao Zhu,¹Yi Zhong,¹Linping Zhang,^1,2Hong Xu ,¹Huaxin Peng,³and Zhiping Mao^1,4,5

Academic Editor: Pierre Verge

Received14 Sept 2021

Revised26 Oct 2021

Accepted09 Nov 2021

Published25 Nov 2021

Abstract

In this study, a kind of inorganic composite flame retardant (Sep@Fe₂O₃) was prepared by combining solution deposition and calcination methods using sepiolite microfiber material as carrier. This inorganic compound flame retardant was combined with waterborne polyurethane (WPU) through layer-by-layer method to prepare WPU composites. The SEM and EDS, TEM, and XRD were used to characterize the microscopic morphology and crystal structure of WPU composites. Thermogravimetric analysis tests confirmed the good thermal stability of WPU/Sep@Fe₂O₃ composites; at the temperature of 600°C, the carbon residual percentage of WPU/Sep, WPU/Fe₂O₃, and WPU/Sep@Fe₂O₃ composites is 7.3%, 12.2%, and 13.4%, respectively, higher than that of WPU (1.4%). Vertical combustion tests proved better flame-retardant property of WPU/Sep@Fe₂O₃ composite-coated cotton than noncoated cotton. The microcalorimeter test proved that the PHRR of WPU/Sep@Fe₂O₃ composites decreased by 61% compared with that of WPU. In addition, after combining with Sep@Fe₂O₃, the breaking strength of WPU increased by 35%.

1. Introduction

As an eco-environmentally polymer material that could replace traditional solvent-based polyurethane, waterborne polyurethane (WPU) has been used more and more widely in producing apparel, clothing, home furnishings, and industrial products in recent years [1, 2]. However, the flammability and poor heat resistance of WPU are a huge obstacle to its application in firefighter’s protective clothing and military and airline industry [3]. Previous research on flame retardant polyurethane has mainly focused on solvent-based polyurethane (PU) [4, 5]. For example, Chen et al. studied on thermal properties of PU nanocomposites based on organic sepiolite [6], but the thermal stability of PU composites is not as good as expect. Zheng et al. researched the characterization of sepiolite/PU nanocomposites [7]; the TG results of sepiolite/PU nanocomposites identified slightly improved. Due to the different dispersion systems of WPU and PU, their molecular structures and properties are also different, leading to the requirements for flame-retardant property also being different. The current situation is that there are a few of studies on the flame-retardant property mainly for WPU. Han et al., Kim et al., and Yeh et al. studied the flame-retardant property of WPU/clay composites; the flame-resistant property of these materials could only be improved a little [8–10].

As society is progressing, human beings become more aware of environmental protection. Even though many conventional flame retardants exhibit excellent flame resistance, halogen-containing flame retardants are banned due to serious environmental problems. Phosphorus- and nitrogen-containing flame retardants as the second category of optional flame retardants still have some environmental problems, such as eutrophication of water caused by the discharge of phosphorus-containing wastewater into the natural world [11–21]. Therefore, there is an urgent need for an environmentally friendly, efficient, and convenient flame retardant.

The researchers proposed that sepiolite- (Sep-) loaded metal oxides could be used for preparing flame-retardant polymer. Sep as a natural silicate material, which is not combustible itself, is nonpolluting to the environment and nonhazardous to human beings. However, when the material is used as flame retardant alone, the flame retardancy is not excellent [22–24]. For these reasons, an inorganic composite flame retardant is prepared by loading the transition metal oxide which has Lewis’s acid property and could act as a kind of catalytic carbon formation agent on Sep. Therefore, this inorganic composite flame retardant could enhance the flame-retardant property of polymer by improving the carbon formation of the substrates. For example, Guillon prepared a series of catalyst which comprised at least one IZM-2 zeolite, one matrix, and one metal selected from metals of groups VIII, VIB, and VIIB. Those catalysts promote rapid thermal decomposition of polymers to generate carbonization [25]. Aranda et al. prepared layered double hydroxide/Sep heterostructured materials and investigated the catalytic properties of the above materials [26]. Yuming Chen and Limin Zhou studied energetics and mechanisms of graphene growth catalyzed by nickel nanoclusters by using ab initio density functional theory calculations [27].

These previous works made believed that loading transition metal oxides into Sep could enhance the carbon-forming effect of Sep. However, what will happen if transition metal oxide is combined with Sep to form a flame-resistant system for WPU? In this study, inorganic composites (Sep@Fe₂O₃) were prepared by combining precipitation and calcination methods to load Fe₂O₃ into Sep crystals; organic/inorganic composites were prepared by combining these inorganic composites with WPU by layer-by-layer (LBL) method to study the thermal stability and combustion properties of these composites and explore the mechanism of the effect of Sep@Fe₂O₃ on the combustion property of WPU.

2. Experimental

2.1. Materials

Sep was obtained from Zhejiang Fenghong Chemical Co., Ltd., China. Both Fe (NO₃)₃·9H₂O (AR) and NaOH (AR) were purchased from Sinopharm Chemical Reagent Co., Ltd., China. WPU (SR-5428) was purchased from Sitoke New Material Co., Ltd., China.

2.2. Preparation of Sep@Fe₂O₃

In this work, Sep@Fe₂O₃ precursor was prepared by dispersing the Sep fiber in deionized water/ethanol (1/1) at 25°C, followed by adding 100 mL Fe (NO₃)₃ solution (0.05 mol/L) with stirring under nitrogen atmosphere for 45 min. In this system, the amount of iron ions is double the cation exchange capacity (CEC) of Sep (93.7 mmol/100 g). Then, 100 mL NaOH solution (0.11 mol/L) was added to the solution with high-speed stirring for 2 h. The slurry aged in the darkroom for 20 min and then was separated by centrifugation (TG20G, Spring Instrument. Co., Ltd., China), washed by deionized water, and dried at 105°C for 4 h. The prepared dry chips were calcinated in muffle furnace (GST-3-1200-I, Shanghai Guangshu Electromechanical Co., Ltd.) at 400°C for 4 h to prepare Sep@Fe₂O₃ composite material.

2.3. Preparation of WPU/Sep@Fe₂O₃ Composites

All films were assembled on a given substrate using the procedure shown in Figure 1. Each substrate was dipped into the deposition mixtures, alternating between the WPU emulsion of 3.0 wt.% and inorganic materials (Sep, Fe₂O₃, and Sep@Fe₂O₃) of 0.2 wt.%, with each cycle corresponding to one bilayer (BL). Each dip was followed by handling with a stream of filtered air for 60 s, the above process was repeated for 10 times, and then WPU composites were prepared. Samples of WPU composites are shown in Table 1.

2.4. Characterization

The microstructure characterization of Sep samples and WPU composites was carried out by X-ray diffractometer (XRD, 6100), transmission electron microscope (TEM, SU-70t), and scanning electron microscopy (SEM, SU-3500). The XRD spectrum of synthesized catalysts was obtained by radiation Cu Ka (). Samples of TEM were embedded in 812 resin (TAAB, UK), and ultrathin sections (about 800 nm thick) were cut on a Leica ultramicrotome (Leica Microsystems, Milton Keynes, UK sections) viewed in a SU-70t TEM. The election high tension (EHT) of SEM was set at 10 kV, and imaging was carried out using SE2 detector. Due to the nonconductive nature of the WPU composites, the samples were sputter-coated with a thin layer of gold prior to the imaging using a Polaron SC 7640 for 60 s. ATR-FTIR spectrophotometry was used to determine the surface structure of the WPU composites and to qualitatively determine the presence of the organic modifiers in the WPU composites. A Tensor 27 model infrared spectrophotometry with attenuated total reflectance module with monolithic diamond crystal for full spectral range from 4000 to 400 cm^-1 was used.

The thermal stability of samples was measured in a thermal gravimetric analyzer (TG, SDT Q600). Each sample was approximately 5 mg and tested from 30°C to 900°C at a heating rate of 20 mL min^-1. The vertical flame test (VFT) was performed according to BG/T 5455-1997, by using a vertical burning tester (BCR-A, Textile Science Institute, Shandong, China). The samples () were prepared using the procedure shown in Figure 1. The above-mentioned substrate for preparing the WPU composite film was changed into cotton textile (115 g/m², Zhuocheng Special Textile Co. Ltd., Xinxiang, China), and we could get cotton-WPU composite materials. Then, the samples held 19 mm over the Bunsen burner were first exposed to the flame for a period of 12 s and then removed rapidly, the test was repeated three times for each sample, and after which, the after-flame and after-glow times were read from the VFT machine.

The combustion performance of samples was determined by a Microscale Combustion Calorimeter (MCC, MCC-2, Govmark, USA) instrument equipped with a 40 μL alumina pan. The samples (~5 mg) were first heated from room temperature to 750°C in an 80 cm³/min nitrogen stream flowing at a linear heating rate of 1°C. Then, the gaseous pyrolysate mixture was mixed with a 20 cm³/min oxygen stream flow and combustion in a furnace at 900°C for 10 s.

Tensile tests of WPU composites were carried out according to standard GB/T 1040.3-2006 on UTM 6203 machine (Shenzhen Sansi Vertical and Horizontal Technology Co., Ltd., China), and the test was repeated 3 times for each sample.

3. Result and Discussion

3.1. Structure Characterization of Samples

3.1.1. Crystal Structure of Samples: XRD Analysis

The results of the XRD test are shown in Figure 2. In the XRD patterns of the Sep and Sep@Fe₂O₃ composites, the characteristic peaks of Sep were weak in the Sep@Fe₂O₃ composites, indicating that the addition of Fe₂O₃ in the Sep@Fe₂O₃ composites affects the reading of the characteristic peak data of Sep [28]. The peak positions of Sep@Fe₂O₃ composites show good agreement to the standard data of Fe₂O₃ structure (PDF: 85-0987, 24.20° represents the characteristic peak of the 110 crystal plane, 35.73° represents that of -110 crystal plane). We observe reflexes associated with the (110) and (-110) planes; the intensity of the (110 crystal plane) reflexes is the highest. This suggests the successful preparation of Sep@Fe₂O₃ composites. In addition, no characteristic peak of other materials is found in XRD patterns, suggesting that the material is the composites of Sep with Fe₂O₃.

The results of crystal characterization of WPU film and WPU/Sep@Fe₂O₃ film are shown in Figure 2. XRD diffraction pattern of WPU film shows a broader diffraction peak, indicating that the WPU film is semicrystalline in nature. The peak at about 22.56°, which is the characteristic peak of WPU, corresponds to the (110) plane of WPU representing scattering from WPU chains at interplanar spacing [29–31]. In addition, the XRD of pure WPU shows the low crystallinity of the sample which is due to repetition of benzenoid rings [32].

The XRD pattern of the WPU/Fe₂O₃ membrane shows peaks at 24.20°, 35.73°, and 62.60°, confirming the presence of Fe₂O₃ nanoparticle within the membrane, indicating the successful incorporation of Fe₂O₃ nanoparticles into the polymer matrix. The XRD pattern of the WPU/Sep@Fe₂O₃ membrane shows the characteristic peaks at 21.67°, 22.42°, 30.73°, and 35.22°, representing the crystalline nature of Sep (PDF: 75-1597). The XRD pattern of the WPU/Sep membrane confirms the presence of Sep within the membrane. The characteristic peaks of Sep are weaker obviously in the WPU/Sep@Fe₂O₃ composites, indicating that the addition of WPU and Fe₂O₃ in the WPU/Sep@Fe₂O₃ composites affects the reading of the characteristic peak data of Sep in XRD.

For WPU compounding with different kinds of inorganic materials, a shift to the right of the crystalline peaks at 21.67° and 22.42° (to 21.80° and 22.48°) is observed. The increase in intensity of the crystalline peaks of WPU composites is attributed to the enhancement of the crystallization portion in the composites caused by the addition of Sep and Fe₂O₃. This indicates that inorganic materials could promote WPU crystallization. The shift in diffraction peak is due to the change in interlayer volume caused by the insertion of inorganic materials into WPU. The increase in crystallinity of WPU composites is due to the intermolecular interaction between the polar groups of iron oxide particles and Sep with the polar group of WPU, which leads to an ordered structure in the polymer matrix.

3.1.2. Surface Morphology and Elemental Analysis of Samples with SEM and EDS

SEM images and EDS analysis data of Sep microfibers and Sep@Fe₂O₃ composites are shown in Figure 3. It can be seen from SEM images of Sep that the Sep microfibers presented in the form of dispersive fibers with a high length-diameter ratio, and there is a distinct difference between Sep and Sep@Fe₂O₃ composites which can be illustrated from the particles covered on the surfaces of Sep microfibers. Combined with EDS data, we could believe that the particles on the Sep are Fe₂O₃ crystals, proving the successful loading of Fe₂O₃ crystals on Sep microfibers.

(a)

(b)

(c)

(d)

(e)

(f)

EDS data of Sep and Sep@Fe₂O₃ composites shows the relative element content of Si, O, Mg, Al, and Fe. The weight percentage of Fe element in Sep@Fe₂O₃ composites is almost 139.5% higher than that in Sep, which also confirms the result that Fe₂O₃ is loaded in Sep microfibers successfully.

3.1.3. Internal Structure of Samples: TEM Studies

Sep structure is shown in Figure 4(a); the nature and location of metallic species within the Sep structure are shown in Figures 4(b) and 4(c). There are several approaches that Fe³⁺ interacts with Sep, which had been purified by HCl in this work. The research has proved that the purified treatment of Sep ore could remove enough Mg²⁺ cations from Sep framework, and then, the Sep could convert to porous silica [33]. In this research, part of Fe³⁺ is incorporated into the magnesium vacancies of Sep to form variety of stable metallic-containing Sep [34, 35]. Once all the magnesium vacancies have been occupied and in case the aqueous solution contains an excess of Fe³⁺, which would precipitate on the Sep surface as crystallized Fe₂O₃ or Fe (OH)₃, this is the case of metal ion interacting via electrostatic attraction. The Sep microfiber is an anionic clay mineral that offers binding sites to immobilize the positively charged particles through electrostatic interactions. In addition, from the TEM image (Figure 4(b)), we could analyze that the diameter of Fe₂O₃ is about 25-70 nm by ImageJ (shown in Figure 5(a)).

(a)

(b)

(c)

(d)

(e)

(f)

(a)

(b)

TEM image analysis can be used to quantify the distribution of Sep fiber lengths and observe the interface of substances with different properties. WPU composite membranes are analyzed by TEM and shown in Figures 4(d)–4(f). In the TEM images of WPU/Sep composite membranes (Figure 4(d)), the Sep fiber bundles completely strip in nanoscale and disperse evenly in the WPU matrix. The TEM image of WPU/Fe₂O₃ membrane (Figure 4(e)) shows that the particle size of Fe₂O₃ crystal is not uniform (shown in nanoscale and micron scale, Figure 5(b)). In addition, there is no obvious phase interface between Fe₂O₃ crystal and WPU matrix. This could prove that the compatibility of organic and inorganic phases is very excellent. TEM of WPU/Sep@Fe₂O₃ composite membrane is shown in Figure 4(f), in which the Fe₂O₃ crystal loaded abundantly on the surface of Sep fibers, which dispersed in the WPU matrix. No phase interface could be found between the interface of Sep and WPU matrix; it means that the two phases (organic and inorganic phases) are compatible. This is manifested in the greater improvement in mechanical and thermal properties which would be discussed in the subsequent sections.

3.2. Properties of Nanocomposites

3.2.1. Thermal Property of Samples: TG

As mentioned in Introduction, we believe that Sep and Fe₂O₃ can be used as flame retardant. Therefore, Sep, Fe₂O₃, and Sep@Fe₂O₃ were used to prepare composites with WPU by LBL method. The TG and DTG thermograms of WPU and WPU composites were analyzed under air atmosphere shown in Figures 6(a) and 6(b). The first stage at 200-300°C involves the elimination reactions of H₂O, CO₂, and NH₃ and residual acetate groups because of partially hydrolyzing of WPU; the degradation step at 300-600°C is more complex and includes the further degradation of WPU residues to yield the carbon and hydrocarbons shown in Figure 6(a). The hydrocarbons in the TGA results have been discussed by our previous studies. The weight loss of WPU/Sep, WPU/Fe₂O₃, and WPU/Sep@Fe₂O₃ composites took place at 300-400°C and 400-600°C, for the loss of structure water of Sep and the thermal decomposition of WPU molecular. As is shown in Figure 6(a), at 600°C, the carbon residual percentages of WPU/Sep, WPU/Fe₂O₃, and WPU/Sep@Fe₂O₃ composites are 7.3%, 12.2%, and 13.4%, respectively, showing obvious difference from the control sample (1.4% for WPU). This increased percentage of char residue implies that Sep, Fe₂O₃, and Sep@Fe₂O₃ are favorable to improve the high-temperature resistance of WPU. Sep could act as the mass transport barrier to the volatiles produced during decomposition. Physi- and/or chemisorption occurring in the filler (Sep and Fe₂O₃)-matrix interphase may lead to the formation of physical network thereby enhancing the nanocomposite stability [7, 36].

(a)

(b)

The DTG (%/min) curves for thermal oxidation of the representative WPU and WPU composite samples are provided in Figure 6(b). Almost all the samples displayed two degradation peaks. It is noteworthy that the temperature at the greatest degradation peaks () decreased from 397°C (for WPU) to 341°C, 378°C, and 366°C, for WPU/Sep, WPU/Fe₂O₃, and WPU/Sep@Fe₂O₃ composites, respectively. This decreasing of is probably due to the catalytic carbonation of Sep and Fe₂O₃ in the WPU composites. This is generally attributed to a catalytic action played by the Lewis acidic sites of clays [37]; Fe₂O₃ itself is a kind of catalyst.

3.2.2. Flame-Retardant Properties of WPU Composites

For the catalytic carbon formation performance of Sep and Fe₂O₃, the flame-retardant property of WPU composites is improved. Considering that cotton fabric is a kind of flammable material and widely used in our daily life, a vertical flammability test was conducted on the coated cotton fabrics. Upon ignition, the noncoated cotton fabrics were burned for about 14 s and had nothing left. The burning time of cotton fabrics coated with WPU composite films is shown in Table 2. The coated cotton fabrics (coated with WPU/Sep film, WPU/Fe₂O₃ film, and WPU/Sep@Fe₂O₃ film) were burned just for 10 s and retained the original fiber structure of the textiles. Shown in Figure 7 are SEM images of cotton residues. From Figures 7(a)–7(c), we could see the integrity of cotton fiber coated with films, which are composed of carbon that converted from WPU films catalyzed by Sep or Fe₂O₃. Benefitting from the protection of WPU composite films, the cotton fabrics could keep their original structure. For these results, we could think that the WPU composite films have the potential to improve the flame-retardant property of cotton fabrics.

(a)

(b)

(c)

(d)

(e)

(f)

3.2.3. Combustion Behavior of WPU Composites

MCC is an effective approach for evaluating the combustion behavior of materials. The heat release rate (HRR) curves versus temperature of WPU and WPU composites are presented in Figure 8. For the WPU film, the thermal decomposition started at approximately 175°C and peaked (418.9 W/g) at 355.2°C. The decomposition of WPU ended at about 385°C. WPU composite films almost started to decompose at approximately 175°C and ended at approximately 485°C. In the presence of the flame-retardant system, the HRR peaked at 355.2°C for the WPU film (shown in Table 3). It increased by 30°C and decreased by 52°C to become two peaks at 385°C (269.9 W/g) and 303°C (241.9 W/g) for the WPU/Sep composite film. As is shown in Table 3, the total heat release (THR) of WPU decreased from 27 to 26 kJ/g whereas the percent char yield of WPU increased from 3.1 to 6.9% after being complexed with Sep. Moreover, the one peak in the HRR curve of the WPU split into two peaks after being complexed with Sep, and the HRR curve of the WPU/Sep composite film became broader with a less symmetric shape than that of WPU. When 6.7 wt.% Sep was replaced by 6.7 wt.% Fe₂O₃ or 6.7 wt.% Sep@Fe₂O₃, peak of heat release rate (pHRR) and THR decreased, and the temperature of heat release rate () has little change. These results demonstrate the formation of a char layer over the surface of the material during the combustion process; the char layer could inhibit gaseous-fuel transport from the WPU to the flame front so as to reduce the HRR of the burning surface according to the combustion mechanism of clay-based composites during the MCC experiments. In addition, the char yield increased from 3.1% (for WPU) to 6.9%, 7.6%, and 14.3% for WPU/Sep, WPU/Fe₂O₃, and WPU/Sep@ Fe₂O₃, respectively, indicating that the addition of inorganic materials could help the WPU to retain more degradation products in the condensed phase during combustion. The data suggested that the flame-retardant property of Sep@Fe₂O₃ is better than that of Sep or Fe₂O₃ alone. In addition, the results of MCC are coincident with the results of TG test (Figure 6(a)).

3.2.4. Tensile Properties

The mechanical properties of WPU and WPU composites are shown in Table 4. The increasing of breaking strength supports the strengthening of mechanical strength, and the decreasing of break elongation indicates the weakening of elasticity of WPU composites. The data presented in the table are the average of three readings. The breaking strength of S-2 decreased from 3.2 N to 2.7 N, as the result of stress concentration due to agglomeration of Sep microfibers. In the case of S-3, breaking strength increased from 3.2 N to 7.0 N, because the addition of Fe₂O₃ into the WPU matrix improved the interfacial adhesion among the WPU matrix through oxygen atoms (in Fe₂O₃ structure) and amino and hydroxyl groups (in WPU molecular structure), respectively [38, 39]. Considering Figure 4(e), the interface between Fe₂O₃ and WPU could not be observed, which means that the compatibility between those two materials is excellent. Therefore, the result of tensile properties of WPU composites is consistent with that of TEM. Sample S-4 was prepared by WPU and Sep@Fe₂O₃, which showed a significant improvement in mechanical property and small reduction in elasticity property. For oxygen atom and hydroxyl in Sep matrix and -NH-, C=O in WPU could form hydrogen bond formation to improve the mechanical strength of WPU composites. Meanwhile, interaction between WPU and inorganic materials could restrict the movement of polymer chains and reduce the elasticity property of WPU composites. In summary, the heat resistance and mechanical properties of WPU/Sep@Fe₂O₃ composites are confirmed in this work, proving that it has the potential to be used as a high temperature-resistant material.

4. Conclusion

In this work, Fe₂O₃ as a kind of flame retardant is loaded in Sep that was used for WPU. Flame-retardant properties of Sep, Fe₂O₃, and Sep@Fe₂O₃ were evaluated by VFT, TGA, and MCC measurements. The compounding of Sep@Fe₂O₃ with WPU could change the thermal stability of the material. Using VFT, it was found that the flame-retardant property achieved optimization when 6.7 wt.% Sep@Fe₂O₃ substituted 6.7 wt.% Sep or Fe₂O₃. In this case, the residual carbon percentages of WPU, WPU/Sep, WPU/Fe₂O₃, and WPU/Sep@Fe₂O₃ composites obtained from TG/DTG curves are 1.4%, 7.3%, 12.2%, and 13.4%, respectively. These results revealed that the thermal stability of WPU/Sep@Fe₂O₃ increased compared with that of WPU/Sep or WPU/Fe₂O₃. This phenomenon can also be observed in the MCC tests in terms of HRC, PHRR, and THR. The values of char yield in TG and MCC tests were higher for samples treated with inorganic flame retardant than those that are untreated. These results show wonderful flame-retardant properties of Sep, Fe₂O₃, and Sep@Fe₂O₃ on WPU materials. Meanwhile, the mechanical property of WPU composites was improved. Therefore, the inorganic flame retardant could be used for preparing flame-retardant WPU composites with improved mechanical property.

Data Availability

The data is included in the manuscript already.

Conflicts of Interest

The authors declared that there are no conflicts of interest in this work. We declare that we do not have any commercial or associative interest that represents a conflict of interest in connection with the work submitted.

Acknowledgments

The present work is supported financially by the National Key R&D Program of China (No. 2018YFC1801500) and the Fundamental Research Funds for the Central Universities (No. 2232020G-04).

References

H. Liang, L. Liu, J. Lu, M. Chen, and C. Zhang, “Castor oil-based cationic waterborne polyurethane dispersions: Storage stability, thermo-physical properties and antibacterial properties,” Industrial Crops and Products, vol. 117, pp. 169–178, 2018.
View at: Publisher Site | Google Scholar
F. Naz, M. Zuber, K. Mehmood Zia et al., “Synthesis and characterization of chitosan-based waterborne polyurethane for textile finishes,” Carbohydrate polymers., vol. 200, pp. 54–62, 2018.
View at: Publisher Site | Google Scholar
R. Patel and P. Kapatel, “Waterborne polyurethanes: A three step synthetic approach towards environmental friendly flame retardant coatings,” Progress in Organic Coating, vol. 125, pp. 186–194, 2018.
View at: Publisher Site | Google Scholar
D. K. Chattopadhyay and D. C. Webster, “Thermal stability and flame retardancy of polyurethanes,” Progress in Polymer Science, vol. 34, no. 10, pp. 1068–1133, 2009.
View at: Publisher Site | Google Scholar
P. M. Visakh, A. O. Semkin, I. A. Rezaev, and A. V. Fateev, “Review on soft polyurethane flame retardant,” Construction and Building Materials, vol. 227, pp. 116673–116679, 2019.
View at: Publisher Site | Google Scholar
H. X. Chen, H. Z. Lu, Y. Zhou, M. S. Zheng, C. M. Ke, and D. L. Zeng, “Study on thermal properties of polyurethane nanocomposites based on organo-sepiolite,” Polymer Degradation and Stability, vol. 97, no. 3, pp. 242–247, 2012.
View at: Publisher Site | Google Scholar
H. X. Chen, M. S. Zheng, H. Y. Sun, and Q. M. Jia, “Characterization and properties of sepiolite/polyurethane nanocomposites,” Materials Science and Engineering A, vol. 445-446, pp. 725–730, 2007.
View at: Publisher Site | Google Scholar
H. Y. Choi, C. Y. Bae, and B. K. Kim, “Nanoclay reinforced UV curable waterborne polyurethane hybrids,” Progress in Organic Coating, vol. 68, no. 4, pp. 356–362, 2010.
View at: Publisher Site | Google Scholar
J. M. Yeh, C. T. Yao, C. F. Hsieh et al., “Preparation, characterization and electrochemical corrosion studies on environmentally friendly waterborne polyurethane/Na+-MMT clay nanocomposite coatings,” European Polymer Journal, vol. 44, no. 10, pp. 3046–3056, 2008.
View at: Publisher Site | Google Scholar
B. K. Kim, J. W. Seo, and H. M. Jeong, “Morphology and properties of waterborne polyurethane/clay nanocomposites,” European Polymer Journal, vol. 39, no. 1, pp. 85–91, 2003.
View at: Publisher Site | Google Scholar
S. Wang, X. Du, Y. Jiang et al., “Synergetic enhancement of mechanical and fire-resistance performance of waterborne polyurethane by introducing two kinds of phosphorus–nitrogen flame retardant,” Journal of Colloid and Interface Science, vol. 537, pp. 197–205, 2019.
View at: Publisher Site | Google Scholar
F. Tabatabaee, M. Khorasani, M. Ebrahimi, A. González, L. Irusta, and H. Sardon, “Synthesis and comprehensive study on industrially relevant flame retardant waterborne polyurethanes based on phosphorus chemistry,” Progress in Organic Coating, vol. 131, pp. 397–406, 2019.
View at: Publisher Site | Google Scholar
G. Wu, J. Li, and Y. Luo, “Flame retardancy and thermal degradation mechanism of a novel post-chain extension flame retardant waterborne polyurethane,” Polymer Degradation and Stability, vol. 123, pp. 36–46, 2016.
View at: Publisher Site | Google Scholar
Y. Ren, Y. Dong, Y. Zhu, J. Xu, and Y. Yao, “Preparation, characterization, and properties of novel ultraviolet-curable and flame-retardant polyurethane acrylate,” Progress in Organic Coating, vol. 129, pp. 309–317, 2019.
View at: Publisher Site | Google Scholar
H. Hu, Y. Yuan, and W. Shi, “Preparation of waterborne hyperbranched polyurethane acrylate/LDH nanocomposite,” Progress in Organic Coating, vol. 75, no. 4, pp. 474–479, 2012.
View at: Publisher Site | Google Scholar
E. Boyles, H. Tan, Y. Wu et al., “Halogenated flame retardants in bobcats from the midwestern United States,” Environmental Pollution, vol. 221, pp. 191–198, 2017.
View at: Publisher Site | Google Scholar
J. de Boer, P. G. Wester, H. J. C. Klamer, W. E. Lewis, and J. P. Boon, “Do flame retardants threaten ocean life?” Nature, vol. 394, no. 6688, pp. 28-29, 1998.
View at: Publisher Site | Google Scholar
L. S. Birnbaum and D. F. Staskal, “Brominated flame retardants: cause for concern?” Health Perspectives, vol. 112, no. 1, pp. 9–17, 2004.
View at: Publisher Site | Google Scholar
X. Chen, C. Ma, and C. Jiao, “Synergistic effects between iron-graphene and ammonium polyphosphate in flame-retardant thermoplastic polyurethane,” Journal of Thermal Analysis and Calorimetry, vol. 126, no. 2, pp. 633–642, 2016.
View at: Publisher Site | Google Scholar
I. van der Veen and J. de Boer, “Phosphorus flame retardants: Properties, production, environmental occurrence, toxicity and analysis,” Chemosphere, vol. 88, no. 10, pp. 1119–1153, 2012.
View at: Publisher Site | Google Scholar
Y. Lu, C. Wu, and S. Xu, “Mechanical, thermal and flame retardant properties of magnesium hydroxide filled poly(vinyl chloride) composites: The effect of filler shape,” Composites. Part A, Applied Science and Manufacturing, vol. 113, pp. 1–11, 2018.
View at: Publisher Site | Google Scholar
V. Carretier, J. Delcroix, M. F. Pucci, P. Rublon, and J. M. Lopez-Cuesta, “Influence of Sepiolite and Lignin as Potential Synergists on Flame Retardant Systems in Polylactide (PLA) and Polyurethane Elastomer (PUE),” Materials, vol. 13, no. 11, pp. 2450–2471, 2020.
View at: Publisher Site | Google Scholar
Y. Pan, L. X. Liu, W. Cai, Y. Hu, S. D. Jiang, and H. T. Zhao, “Effect of layer-by-layer self-assembled sepiolite-based nanocoating on flame retardant and smoke suppressant properties of flexible polyurethane foam,” Applied Clay Science, vol. 168, pp. 230–236, 2019.
View at: Publisher Site | Google Scholar
S. Pappalardo, P. Russo, D. Acierno, S. Rabe, and B. Schartel, “The synergistic effect of organically modified sepiolite in intumescent flame retardant polypropylene,” European Polymer Journal, vol. 76, pp. 196–207, 2016.
View at: Publisher Site | Google Scholar
“Guillon,” U.S. Patent 8, 629, 073B2, 2014.
View at: Google Scholar
A. Gómez-Avilés, P. Aranda, and E. Ruiz-Hitzky, “Layered double hydroxide/sepiolite heterostructured materials,” Applied Clay Science, vol. 130, pp. 83–92, 2016.
View at: Publisher Site | Google Scholar
Y. Chen, J. Dong, L. Qiu, J. K. Kim, F. Ding, and L. Zhou, “A catalytic etching-wetting-dewetting mechanism in the formation of hollow graphitic carbon fiber,” Chem, vol. 2, pp. 299–310, 2017.
View at: Google Scholar
D. H. Taffa, I. Hamm, C. Dunkel, I. Sinev, D. W. Bahnemann, and M. Wark, “Electrochemical deposition of Fe2O3in the presence of organic additives: a route to enhanced photoactivity,” RSC Advances, vol. 5, no. 125, pp. 103512–103522, 2015.
View at: Publisher Site | Google Scholar
A. Biswas, I. S. Bayer, P. C. Karulkar, A. Tripathi, and D. K. Avasthi, “Vapor-phase deposition of regioregular and oriented poly(3-hexylthiophene) structures and novel nanostructured composites of interpenetrating poly(3-hexylthiophene) and polyaniline exhibiting full-color wavelength (400–1000nm) photoluminescence,” Journal of Applied Physics, vol. 102, no. 8, pp. 083543–083548, 2007.
View at: Publisher Site | Google Scholar
S. Min, F. Wang, and Y. Han, “An investigation on synthesis and photocatalytic activity of polyaniline sensitized nanocrystalline TiO2 composites,” Journal of Materials Science, vol. 42, no. 24, pp. 9966–9972, 2007.
View at: Publisher Site | Google Scholar
W. Feng, E. Sun, A. Fujii, H. Wu, K. Niihara, and K. Yoshino, “Synthesis and Characterization of Photoconducting Polyaniline-TiO2Nanocomposite,” Bulletin of the Chemical Society of Japan, vol. 73, no. 11, pp. 2627–2633, 2000.
View at: Publisher Site | Google Scholar
J. W. Zhang, Y. Li, and S. Zhang, “Preparation, Characterization and Corrosion Evaluation of Poly(o-toluidine), Poly(m-Toluidine), and Poly(p-Toluidine) Blended with Waterborne Polyurethane,” Journal of Metals, vol. 70, no. 11, pp. 2660–2666, 2018.
View at: Publisher Site | Google Scholar
C. H. Zhou, G. L. Li, X. Y. Zhuang et al., “Roles of texture and acidity of acid-activated sepiolite catalysts in gas-phase catalytic dehydration of glycerol to acrolein,” Molecular Catalysis, vol. 434, pp. 219–231, 2017.
View at: Publisher Site | Google Scholar
A. Corma, J. Perez-Pariente, and J. Soria, “Physico-chemical characterization of Cu2+-exchanged sepiolite,” Clay Minerals, vol. 20, no. 4, pp. 467–475, 1985.
View at: Publisher Site | Google Scholar
V. Li, “Acid–base behaviour and Cu2+ and Zn2+ complexation properties of the sepiolite/water interface,” Chemical Geology, vol. 198, no. 3-4, pp. 213–222, 2003.
View at: Publisher Site | Google Scholar
F. Chivrac, E. Pollet, M. Schmutz, and L. Avérous, “Starch nano-biocomposites based on needle-like sepiolite clays,” Carbohydrate Polymers, vol. 80, no. 1, pp. 145–153, 2010.
View at: Publisher Site | Google Scholar
F. Bellucci, G. Camino, A. Frache, and A. Sarra, “Catalytic charring–volatilization competition in organoclay nanocomposites,” Polymer Degradation and Stability, vol. 92, no. 3, pp. 425–436, 2007.
View at: Publisher Site | Google Scholar
X. Zou, B. Sariyev, K. Chen et al., “Enhanced interfacial bonding strength between metal and polymer via synergistic effects of particle anchoring and chemical bonding,” Journal of Manufacturing Processes, vol. 68, pp. 558–568, 2021.
View at: Publisher Site | Google Scholar
R. K. Naik, S. K. Panda, and V. Racherla, “A new method for joining metal and polymer sheets in sandwich panels for highly improved interface strength,” Composite Structures, vol. 251, pp. 112661–112668, 2020.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2021 Tong Xu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

529

Downloads

611

Citations

Advances in Polymer Technology

Effect of Sepiolite-Loaded Fe2O3 on Flame Retardancy of Waterborne Polyurethane

Abstract

1. Introduction

2. Experimental

2.1. Materials

2.2. Preparation of Sep@Fe2O3

2.3. Preparation of WPU/Sep@Fe2O3 Composites

2.4. Characterization

3. Result and Discussion

3.1. Structure Characterization of Samples

3.1.1. Crystal Structure of Samples: XRD Analysis

3.1.2. Surface Morphology and Elemental Analysis of Samples with SEM and EDS

3.1.3. Internal Structure of Samples: TEM Studies

3.2. Properties of Nanocomposites

3.2.1. Thermal Property of Samples: TG

3.2.2. Flame-Retardant Properties of WPU Composites

3.2.3. Combustion Behavior of WPU Composites

3.2.4. Tensile Properties

4. Conclusion

Data Availability

Conflicts of Interest

Acknowledgments

References

Copyright

Effect of Sepiolite-Loaded Fe₂O₃ on Flame Retardancy of Waterborne Polyurethane

2.2. Preparation of Sep@Fe₂O₃

2.3. Preparation of WPU/Sep@Fe₂O₃ Composites