Abstract

A new organic charge transfer molecular complex salt of benzimidazolium salicylate (BSL) single crystals was grown by the slow evaporation solution growth technique using methanol as a solvent at room temperature. The grown crystals were characterised by single crystal X-ray diffraction (XRD) which confirms that the crystal belongs to monoclinic system with the centrosymmetric space group P21/. The crystalline perfection of the grown crystal was analyzed by high resolution X-ray diffraction (HRXRD). The presence of various functional groups was identified by FTIR spectrum. UV-Vis spectral study reveals that the BSL crystal is optically transparent in the wavelength region 342 nm–1100 nm. Dielectric measurements of the crystal at various frequencies were also determined. The mechanical properties of the grown crystal were assessed using Vickers microhardness testing. Nonlinear optical property of the crystal was confirmed using Kurtz and Perry powder technique and the SHG efficiency of the BSL crystal is 0.7 times greater than that of the standard KDP crystal.

1. Introduction

In recent years, organic materials have attracted many researchers due to its high nonlinearities, ultrafast response in electrooptic effect, large optical susceptibilities, large second order molecular polarizability, and higher resistance to optical damage and they have wide applications in optical communications, frequency mixing, optical parametric oscillation, information storage, and so forth [14]. According to crystal engineering, second harmonic generation occurs mostly in noncentrosymmetric crystals due to nonzero hyperpolarizability. But some of the recent reports of organic molecular complexes like caffenium picrate [5], picolinium maleate [6], guanidinium trifluoroacetate, and so forth have highlighted that even centrosymmetric crystals possess SHG effect due to the presence of delocalized electron system linking donor and acceptor groups which enhance the necessary asymmetric polarizability [7, 8]. The various organic subnetworks enhance the thermal and mechanical stabilities through hydrogen bonding interactions and behave as noncentrosymmetry material in the bulk [9, 10]. In organic molecular charge transfer complexes, the charge transfer interaction and molecular aggregation through intermolecular hydrogen bonding has been entrenched by single crystal XRD analysis [11, 12].

Benzimidazole is a very good proton acceptor and, in the presence of a carboxylic acid, it will always deprotonate that group. Hence it is widely used in the formation of organic molecular complex salts like benzimidazolium hydrogen phenylmalonate, benzimidazolium hydrogen nitroterepthalate, 2 methyl benzimidazolium picrate, and so forth [1315]. According to Mulliken, the charge transfer interactions between two aromatic molecules arise due to the transfer of an electron from Lewis base to Lewis acid and have attracted considerable attention on these complexes for their nonlinear optical properties [16, 17]. The researchers have reported recently Benzimidazole based organic compounds with good nonlinear properties such as 1H benzimidazolium hydrogen L-tartrate dihydrate [18], benzil doped Benzimidazole [19], benzimidazolium per chlorate [20]. Similarly salicylic acid forms salicylate salts with various organic molecules and forms salts through hydrogen bonding interactions like Urea salicylate, Bis Guanidinium 5 sulfosalicylate, and Brucinium 5 sulfosalicylate trihydrate and they are reported as efficient NLO materials [2123]. The formation of hydrogen bonding in benzimidazolium organic complex salts was reported. In the present work, the Benzimidazole molecule is protonated through hydrogen transfer from the carboxylic group on the 2-hydroxy benzoic acid (salicylic acid). In this paper the synthesis, crystal growth, and structural, spectral, optical, and mechanical properties of the benzimidazolium salicylate (BSL) crystal for NLO applications are reported.

2. Materials and Methods

2.1. Synthesis and Crystal Growth

Analar grade Benzimidazole and salicylic acid were taken in 1 : 1 molar ratio and dissolved completely in methanol. The mixture was stirred well for about 6 hrs. The reaction involved is illustrated in Figure 1. Suspended impurities were removed by using Whatman 41 grade filter paper. The clear filtrate so obtained was kept aside in a dust-free room for the growth of single crystal. The purity of synthesized compound BSL was improved by successive recrystallization process and filtration. Optically good transparent, colourless crystal having dimensions 19 × 9 × 4 mm3 with perfect external morphology was harvested within a period of 1 week and the grown crystal is shown in Figure 2.

3. Characterization Studies

3.1. Single Crystal X-Ray Diffraction Studies

Single crystal X-ray diffraction analysis of the grown crystal was carried out using ENRAF NONIUS CAD-4 X-ray diffractometer equipped with monochromated MoK radiation ( Å). It is found that the crystal belongs to monoclinic crystal system with space group P21/. The crystal data and the structure refinement for BSL crystal is given in Table 1. The structure of the BSL crystal has been solved by direct methods and refined by full-matrix least square techniques using SHELXL-97 program to an value of 0.0481. The ORTEP diagram of the molecular structure of the grown BSL single crystal is shown in Figure 3. The title salt consists of a cation and anion in the asymmetric unit. The cation is protonated at N atom. The dihedral angle between the benzimidazolium and benzene rings is 75.88(5)°. The molecular structure is stabilized by weak O---H…O hydrogen bond which generates S(6) graph-set motif. In the crystal structure, the weak intermolecular N---H…O, C---H…O hydrogen bonds link the adjacent anions and cations. The crystal packing is further influenced by weak C-H…Π and Π…Π [Cg1…Cg1(i) distance = 3.4156(7) Å; Cg1…Cg2(ii) distance = 3.8196(8) Å; (i) ; (ii) ; Cg1 and Cg2 are the centroids of the rings (N1/C8/C13/N2/C14) and (C8–C13), resp.] interactions, forming a three-dimensional network.

3.2. High-Resolution X-Ray Diffractometry (HRXRD) Analysis

The rocking curves of the BSL crystals for the diffraction planes (0 0 1) were recorded in symmetrical Bragg geometry using the natural facets by performing scan with double-axis geometry [24]. The monochromated X-ray beam incident on the specimen was obtained using a high-resolution four-bounce Ge (2 2 0) monochromator. A scintillation detector was used to record the diffracted beam from the crystal sample without using any analyzer at the receiving stage before the detector to get all the possible information like the individual peaks from structural grain boundaries, scattered intensity from the dislocations, and other defects from the specimen crystal. Figure 4 shows the recorded high resolution X-ray diffraction curve for a typical BSL crystal specimen using (0 0 1) diffracting planes in symmetrical Bragg geometry by employing the multicrystal X-ray diffractometer with MoK1 radiation. The DC contains a single peak and indicates that the specimen is free from structural grain boundaries. The FWHM (full width at half maximum) of the curve is 158 arcsec which is close to the perfect real life crystal. The low values of FWHM and the low angular spread of around 500 arcsec of the DC indicate that the crystalline perfection is reasonably good. Growth conditions as well as thermodynamic considerations also result in point defects in the crystals and are unavoidable up to some extent [25].

3.3. FT-IR Spectrum

The FT-IR spectrum of benzimidazolium salicylate was recorded in the range 4000–400 cm−1 (Figure 5). It is evident from the spectrum that the band at 3339 cm−1 is assigned to the OH asymmetric stretching vibration. The bands at 3082 and 2988 cm−1 are due to aromatic C-H asymmetric and symmetric stretching vibrations of Benzimidazole, respectively. The C=O vibration of COO in salicylate gives its peak at 1620 cm−1. In free salicylic acid C=O vibration occurs at 1750 cm−1. The shift towards low value, therefore, illustrates the transfer of carboxylic proton from carboxylic acid to Benzimidazole. The bands at 1592, 1478, 1451, and 1380 cm−1 are assigned to the aromatic C=C stretching vibrations of Benzimidazole ring which once again verifies the presence of Benzimidazole in the crystal [26]. The band observed at 1139 cm−1 is assigned to C-H inplane bending vibration of benzimidazolium ring [27]. The band at 1353 cm−1 is due to C-H bending. A band at 1244 cm−1 is assigned to the C-O stretching vibration. The bands at 1029 and 932 cm−1 are assigned to C-N stretching vibration. The band at 766 cm−1 is due to the C-H out of plane bending of aromatic hydrogen atom. The respective assignments are given in Table 2.

3.4. UV-Vis Absorption Spectral Analysis

The UV-Vis spectrum relinquishes valuable information about the atomic structure of the molecules because the absorption of UV and visible light involves the promotion of and orbital electrons from the ground state to higher energy state. For device fabrication, this is one of the desirable properties of the crystals. The electronic absorption spectrum of BSL crystal was recorded using Shimadzu 1601 UV-Vis spectrophotometer in the range 200–1100 nm and is shown in Figure 6. The optical absorption spectrum indicates that the crystal has lower cut-off wavelength of about 342 nm. From the absorption spectrum, it can be observed that there is less absorbance in the entire visible and near-infrared region. The wide transparency and lower cut-off is one of the requirements for having efficient NLO character. The absorption due to electronic transitions above 300 nm is the key requirement for frequency doubling using diode and solid state lasers [28]. The absorption peak at 342 nm is assigned to to transition of the compound which is attributed to the charge transfer of the compound. Absence of absorption between 400 nm and 800 nm is the key requirement for materials possessing SHG properties. Thus BSL crystal can be used as a potential candidate for the SHG device application in the visible region [29]. The UV cut-off wavelength of BSL is comparable with other Benzimidazole derivatives such as benzimidazolium per chlorate (360 nm) and pure Benzimidazole (300 nm) and salicylic acid salts like Brucinium 5 sulfosalicylate (312 nm), Urea salicylic acid (347 nm), and so forth [1821, 30].

3.5. Determination of Optical Band Gap

The optical absorption coefficient () was calculated from the transmittance using, where is the transmittance and is the thickness of the crystal. The plot of variation of versus is shown in Figure 7. The band gap energy is evaluated by the extrapolation of the linear part. The band gap was found to be 3.07 eV. The transmittance increases while the band gap becomes wider. The wide band gap energy confirms the good optical transparency and dielectric behaviour of the crystal [31]. It also ensures the crystal suitability for optoelectronic device application, optical harmonic generation, and so forth [32].

3.6. Dielectric Studies

The capacitance () and dielectric loss were measured using the conventional parallel plate capacitor connected with HIOKI-LCR Hi-Tester 3532 at temperatures 308 K, 318 K, and 328 K with frequency range of 50 Hz to 6 MHz. The dielectric studies of BSL crystal was performed with a crystal of dimension 19 × 9 × 4 mm3 which was coated with good quality graphite to obtain a good conductive surface layer. The variation of dielectric constant and dielectric loss as a function of at different temperatures are shown in Figures 8 and 9.

It is observed from Figure 8 that the dielectric constant decreases with increasing frequency and finally it becomes almost a constant at higher frequencies for all temperatures. The dielectric constant has a high value of 505 at 100 Hz and decreases to 23 at 6 MHz. The higher value of dielectric constant at lower frequency region may be due to the presence of all the four types of polarization, namely, space charge, orientation, and ionic and electronic polarizations. The lower value of dielectric constant at higher frequency was due to the loss of significance of these polarizations gradually. Space charge polarization is generally active at lower frequencies and high temperatures which signifies the perfection of the crystal. The variation of dielectric loss at different frequencies and temperatures (Figure 9) shows the same trend as dielectric constant. The crystal undergoes piezoelectric resonance at 10 KHz where the frequency of the electric field matches the frequency of the vibration of the crystal [33]. Also the temperature dependence of dielectric constant and dielectric loss can be explained as being due to temperature dependence of protonic movement and ionic polarizability [34]. The considerable low value of dielectric constant at higher frequencies indicates that the crystal can be used in photonic, electrooptic, and NLO devices. Moreover the low dielectric losses at higher frequencies indicate that the grown BSL crystal is of good quality with lesser defects and is an important parameter for nonlinear optical material in their applications [35].

The alternating current conductivity is calculated using the relation [36]where is the frequency of the applied ac field (Hz), is the permittivity of free space, and and are the measured values of dielectric constant and dielectric loss of the material. The ac conductivity plot with temperature for varying frequency is shown in Figure 10. This plot shows that the ac conductivity increases with frequency and temperature which indicates the normal dielectric behaviour of BSL crystal.

3.7. Vickers Microhardness Analysis

The mechanical properties of crystals are determined by mechanical testing which enables us to study the mechanical characteristics of crystals. The Vickers microhardness study was made on the as grown face of BSL for the static indentation test in air at room temperature using Leitz Wetzlar hardness tester fitted with Vickers diamond pyramidal indentor. The Vickers hardness number was calculated using the expressionwhere is the Vickers hardness number for a given load, , in gram and is the average diagonal length of the indentation in mm. For loads ranging from 25 to 100 gm, the microhardness values of BSL were found to be increasing with load. The plot of versus load is shown in Figure 11. The Mayer index number was calculated from Mayer’s law which relates the load and indentation diagonal length. Considerwhere is the material constant and is work-hardening coefficient. The plot between and is shown in Figure 12. According to Onitsch should lie between 1 and 1.6 for harder materials and above 1.6 for softer materials [37]. The work-hardening coefficient () was calculated to be 3.389 from the slope of versus . Thus the BSL crystal belongs to soft material category.

3.8. SHG Efficiency Analysis

The SHG conversion efficiency of benzimidazolium salicylate was determined by Kurtz’s Perry technique. The crystal was ground into a very fine powder and tightly packed in a microcapillary tube. Then it was mounted in the path of Nd:YAG laser beam of energy 1.9 mJ/s. The output of 44 mV was obtained for the grown sample. When KDP crystal of the same size was used as a reference material an output of 64 mV was obtained. Hence the grown crystal has an efficiency of about 0.7 times greater than that of KDP.

The criteria for SHG may also be satisfied by centrosymmetric molecule if they aggregate in a noncentrosymmetric manner and there is a contribution to the bulk susceptibility from intermolecular charge transfer [5]. Most molecules like paranitro aniline have very large SHG at the molecular scale due to the charge transfer from the donor to the acceptor crystallize in a centrosymmetric lattice due to predominating antiparallel -stacking between the aromatic rings as a consequence of dipolar interactions [42, 43]. Even though the material belongs to centrosymmetric it exhibits SHG activity due to intermolecular hydrogen bonding and charge transfer interactions between the donor and acceptor systems. The SHG in BSL crystal is due to weak interaction between the dipoles, which is easy for the ground state to turn into the excited state as a charge separated form and generate the stable asymmetrical distribution of electron cloud density thus exhibiting a minimum SHG effect [44, 45]. The SHG efficiency of BSL crystal is compared with other reported SHG efficiencies of centrosymmetric materials and is tabulated in Table 3.

4. Conclusion

The organic molecular complex salt BSL was synthesized and grown as single crystal by slow evaporation solution growth technique at room temperature with methanol as the solvent. The single crystal XRD confirms that the BSL crystal belongs to monoclinic system with the centrosymmetric space group P21/. The functional groups present in the grown crystal have been confirmed by FT-IR spectral analysis. The UV-Vis spectral analysis reveals high transparency of BSL crystal in the entire visible region. The optical band gap energy () of the BSL crystal is 3.07 eV. The mechanical stability of BSL was determined using Vickers microhardness analysis. The high resolution X-ray diffraction (HRXRD) of the crystal shows that the perfection of the crystal is quite good. Dielectric measurements were carried out to analyse the dielectric constant and dielectric loss at different frequencies and at different temperature. The powder SHG efficiency of BSL is 0.7 times that of KDP. The SHG effect from the centrosymmetric crystal is a remarkable experimental observation and it is concluded that BSL is a potential material for photonic device fabrication.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

The authors thank Professor P. K. Das, Department of Inorganic and Physical Chemistry, IISC, Bangalore, for the measurement of powder SHG efficiency.