Study on the Microstructure of Vanadium-Modified Tungsten High-Speed Steel-Coded SAE-AISI T1 Steel
Table 8
Chemical composition of the matrix for T1 high-speed tool steel and its different variants (as solidified).
| Steel designation | State | Chemical composition, wt. % | C | Cr | V | W | Mo | Si | Fe |
| Standard T1 high-speed tool steel | T1 high speed | Calculated | 1.71E − 03 | 2.95 | 0.11 | 0.87 | 0.06 | 0.28 | 95.73 | Measured | 5.27E − 06 | 3.00 | 0.2 | 1.5 | 0.10 | 0.30 | 95.3 |
| Vanadium-modified T1 high-speed tool steel | 2 V-13W | Calculated | 1.43E − 03 | 3.38 | 0.15 | 0.94 | 0.08 | 0.25 | 95.19 | Measured | 3.94E − 06 | 2.635 | 0.11 | 0.245 | — | 0.22 | 97.011 | 3V-8W | Calculated | 1.10E − 03 | 4.14 | 0.23 | 1.05 | 0.12 | 0.23 | 94.23 | Measured | 3.13E − 06 | 3.309 | 0.166 | 0.27 | 0.15 | 0.21 | 96.255 | 4V-3W | Calculated | 5.03E − 04 | 4.20 | 0.50 | 1.17 | 0.23 | 0.22 | 93.69 | Measured | 2.43E − 06 | 4.272 | 0.278 | 0.288 | 0.27 | 0.22 | 95.16 |
| Vanadium with extra carbon-modified T1 high-speed tool steel | 2V-13W-HC | Calculated | 2.30E − 03 | 2.30 | 0.07 | 0.76 | 0.06 | 0.26 | 96.55 | Measured | 1.01E − 05 | 1.35 | 0.031 | 0.161 | — | 0.24 | 98.46 | 3V-8W-HC | Calculated | 2.70E − 03 | 2.02 | 0.06 | 0.71 | 0.05 | 0.24 | 96.91 | Measured | 1.84E − 05 | 0.94 | 0.015 | 0.125 | — | 0.21 | 98.92 | 4V-3W-HC | Calculated | 4.54E − 03 | 1.34 | 0.03 | 0.35 | 0.05 | 0.23 | 97.99 | Measured | 3.64E − 03 | 1.65 | 0.049 | 0.539 | — | 0.22 | 97.75 |
|
|