Study on the Effect of Different Fe<sub>2</sub>O<sub>3</sub>/ZrO<sub>2</sub> Ratio on the Properties of Silicate Glass Fibers

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="7"><hr/></td></tr><tr class="thead"><td class="align_left">Sample</td><td class="align_center">1#</td><td class="align_center">2#</td><td class="align_center">3#</td><td class="align_center">4#</td><td class="align_center">E-glass</td><td class="align_center">AR-glass</td></tr><tr><td class="thead-hr" colspan="7"><hr/></td></tr><tr><td class="align_left"><svg height="12.1436pt" id="M15" style="vertical-align:-3.18148pt" version="1.1" viewbox="-0.0498162 -8.96212 12.249 12.1436" width="12.249pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M620 675H597C578 656 570 650 541 650H144C112 650 104 653 94 675H72C59 618 42 552 23 493L53 491C71 534 88 564 105 585C124 608 144 615 238 615H290L197 121C182 40 174 34 88 28L82 0H361L367 28C275 34 266 38 281 121L374 615H441C522 615 543 608 553 583C562 560 566 531 565 493L597 494C603 551 612 629 620 675Z" id="g113-85"></path></g><g transform="matrix(.0091,0,0,-0.0091,7.176,3.132)"><path d="M389 0V32C297 38 291 46 291 118V635C234 613 175 595 109 583V556L161 554C203 552 207 547 207 497V118C207 46 201 38 110 32V0H389Z" id="g50-50"></path></g></svg>/MPa</td><td class="align_center">2936.72</td><td class="align_center">2798.74</td><td class="align_center">2240.21</td><td class="align_center">1804.86</td><td class="align_center">2340.27</td><td class="align_center">2417.90</td></tr><tr><td class="align_left"><svg height="12.1436pt" id="M16" style="vertical-align:-3.18148pt" version="1.1" viewbox="-0.0498162 -8.96212 12.249 12.1436" width="12.249pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M620 675H597C578 656 570 650 541 650H144C112 650 104 653 94 675H72C59 618 42 552 23 493L53 491C71 534 88 564 105 585C124 608 144 615 238 615H290L197 121C182 40 174 34 88 28L82 0H361L367 28C275 34 266 38 281 121L374 615H441C522 615 543 608 553 583C562 560 566 531 565 493L597 494C603 551 612 629 620 675Z" id="g113-85"></path></g><g transform="matrix(.0091,0,0,-0.0091,7.176,3.132)"><path d="M414 144C384 79 371 75 317 75H135L276 221C367 316 408 376 408 465C408 570 327 635 237 635C179 635 131 609 100 575L42 494L67 471C94 510 138 565 205 565C277 565 321 517 321 435C321 348 258 270 195 195C146 137 88 81 33 26V0H411C423 44 433 88 446 135L414 144Z" id="g50-51"></path></g></svg>/MPa</td><td class="align_center">2780.49</td><td class="align_center">2468.69</td><td class="align_center">1889.44</td><td class="align_center">1338.11</td><td class="align_center">1538.56</td><td class="align_center">2032.74</td></tr><tr><td class="align_left">Strength retention rate/%</td><td class="align_center">94.68</td><td class="align_center">88.21</td><td class="align_center">84.34</td><td class="align_center">74.14</td><td class="align_center">65.74</td><td class="align_center">84.07</td></tr><tr class="table-tr"><td colspan="7"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Tensile strength and strength retention rate of samples before and after corrosion in saturated Ca(OH)<sub>2</sub> solution.

Advances in Materials Science and Engineering

tab3

Table 3

Table 3: Study on the Effect of Different Fe<sub>2</sub>O<sub>3</sub>/ZrO<sub>2</sub> Ratio on the Properties of Silicate Glass Fibers 

Advances in Materials Science and Engineering

Study on the Effect of Different Fe2O3/ZrO2 Ratio on the Properties of Silicate Glass Fibers

Table 3

Study on the Effect of Different Fe₂O₃/ZrO₂ Ratio on the Properties of Silicate Glass Fibers