Preparation, Characterization, and Evaluation of Humidity-Dependent Electrical Properties of Undoped and Niobium Oxide-Doped TiO2 : WO3 Mixed Powders
Table 4
Fit parameters for presented Nyquist plots of the sensor TiW-Nb6 at 20°C.
| RH (%) | R1 (Ω) | C1 (F) | R2 (Ω) | C2 (F) | R3 (Ω) | C3 (F) | Cgeo (F) | Ael (Ω−1) | nel | Apo (Ω−1) | npo | Asup (Ω−1) | nsup | Rsup (Ω) |
| 10 | 1.0E + 5 | 5.0E − 11 | 1.81E + 5 | 6.0E − 11 | 6.0E + 4 | 9.0E − 11 | 3.0E − 11 | 2.22E − 9 | 5.45E − 1 | 6.4E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 7.0E + 3 | 20 | 1.11E + 5 | 5.0E − 11 | 2.03E + 5 | 5.0E − 11 | 6.0E + 4 | 9.0E − 11 | 3.0E − 11 | 2.22E − 9 | 5.45E − 1 | 6.4E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 7.0E + 3 | 30 | 1.01E + 5 | 3.0E − 11 | 1.99E + 5 | 3.0E − 11 | 6.0E + 4 | 9.0E − 11 | 3.0E − 11 | 2.22E − 9 | 5.45E − 1 | 6.4E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 7.0E + 3 | 40 | 9.4E + 4 | 1.0E − 10 | 2.72E + 5 | 4.0E − 11 | 1.2E + 4 | 2.0E − 8 | 2.0E − 11 | 3.8E − 9 | 5.55E − 1 | 2.0E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 7.0E + 3 | 50 | 8.4E + 4 | 1.0E − 10 | 2.45E + 5 | 4.0E − 11 | 2.4E + 4 | 7.0E − 9 | 2.0E − 11 | 5.0E − 9 | 5.55E − 1 | 2.0E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 7.0E + 3 | 60 | 8.5E + 4 | 1.3E − 10 | 2.4E + 5 | 5.0E − 11 | 5.3E + 4 | 2.7E − 9 | 5.0E − 12 | 4.9E − 9 | 5.55E − 1 | 3.0E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 1.8E + 4 | 70 | 5.5E + 4 | 1.3E − 10 | 2.1E + 5 | 3.9E − 11 | 6.6E + 4 | 1.4E − 9 | 3.0E − 12 | 4.5E − 9 | 5.58E − 1 | 3.0E − 9 | 6.2E − 1 | 9.E − 11 | 9.0E − 1 | 1.4E + 4 | 80 | 4.8E + 4 | 1.3E − 10 | 1.66E + 5 | 3.9E − 11 | 9.3E + 4 | 7.0E − 10 | 3.0E − 12 | 9.0E − 9 | 5.58E − 1 | 2.8E − 9 | 6.2E − 1 | 1.E − 12 | 9.0E − 1 | 2.4E + 4 | 90 | 4.8E + 4 | 1.3E − 10 | 1.69E + 5 | 3.9E − 11 | 8.7E + 4 | 7.9E − 10 | 3.0E − 12 | 8.0E − 9 | 5.58E − 1 | 2.8E − 9 | 6.2E − 1 | 1.E − 12 | 9.0E − 1 | 1.4E + 4 | 100 | 4.1E + 4 | 1.8E − 10 | 1.17E + 5 | 3.7E − 11 | 9.7E + 4 | 4.8E − 10 | 1.0E − 12 | 2.0E − 8 | 5.58E − 1 | 2.9E − 9 | 6.2E − 1 | 2.E − 11 | 9.0E − 1 | 4.1E + 4 |
|
|