Preparation, Characterization, and Evaluation of Humidity-Dependent Electrical Properties of Undoped and Niobium Oxide-Doped TiO2 : WO3 Mixed Powders
Table 2
Fit parameters for presented Nyquist plots of the sensor TiW-Nb2 at 20°C.
| RH (%) | R1 (Ω) | C1 (F) | R2 (Ω) | C2 (F) | R3 (Ω) | C3 (F) | Cgeo (F) | Ael (Ω−1) | nel | Apo (Ω−1) | npo | Asup (Ω−1) | nsup | Rsup (Ω) |
| 10 | 6.0E + 5 | 3.1E − 10 | 1.89E + 6 | 1.1E − 11 | 9.9E + 4 | 6.0E − 11 | 1.43E − 11 | 2.22E − 9 | 5.2E − 1 | 6.0E − 9 | 6.1E − 1 | 9.0E − 12 | 9.9E − 1 | 9.0E + 4 | 20 | 4.7E + 5 | 5.8E − 10 | 1.93E + 6 | 1.55E − 11 | 9.9E + 4 | 6.0E − 11 | 1.4E − 11 | 2.22E − 9 | 5.16E − 1 | 6.4E − 9 | 6.1E − 1 | 9.0E − 12 | 9.9E − 1 | 8.0E + 4 | 30 | 3.6E + 5 | 5.8E − 10 | 1.47E + 6 | 1.55E − 11 | 9.9E + 4 | 6.0E − 11 | 1.4E − 11 | 2.22E − 9 | 5.2E − 1 | 6.4E − 9 | 6.1E − 1 | 9.0E − 12 | 9.9E − 1 | 5.0E + 4 | 40 | 6.8E + 5 | 7.0E − 11 | 8.30E + 5 | 8.0E − 12 | 9.9E + 4 | 6.0E − 11 | 1.6E − 12 | 2.5E − 9 | 5.18E − 1 | 3.9E − 9 | 6.15E − 1 | 9.0E − 12 | 9.9E − 1 | 6.5E + 4 | 50 | 5.8E + 5 | 7.0E − 11 | 5.80E + 5 | 8.9E − 12 | 1.04E + 5 | 6.0E − 11 | 2.0E − 12 | 2.5E − 9 | 5.3E − 1 | 3.9E − 9 | 6.15E − 1 | 5.47E − 12 | 9.9E − 1 | 3.9E + 4 | 60 | 4.3E + 5 | 8.0E − 11 | 4.00E + 5 | 8.9E − 12 | 1.04E + 5 | 6.0E − 11 | 2.7E − 12 | 2.5E − 9 | 5.4E − 1 | 3.9E − 9 | 6.15E − 1 | 5.47E − 12 | 9.9E − 1 | 3.3E + 4 | 70 | 3.25E + 5 | 8.0E − 11 | 2.57E + 5 | 8.9E − 12 | 1.08E + 5 | 5.0E − 11 | 2.0E − 12 | 2.5E − 9 | 5.43E − 1 | 3.9E − 9 | 6.15E − 1 | 5.47E − 9 | 5.0E − 1 | 1.3E + 4 | 80 | 2.6E + 5 | 8.0E − 11 | 1.70E + 5 | 8.9E − 12 | 1.05E + 5 | 4.7E − 11 | 8.0E − 13 | 2.5E − 9 | 5.43E − 1 | 6.0E − 9 | 6.23E − 1 | 5.47E − 9 | 5.0E − 1 | 9.0E + 3 | 90 | 2.0E + 5 | 9.0E − 11 | 1.27E + 5 | 8.9E − 12 | 1.0E + 5 | 4.7E − 11 | 5.0E − 13 | 2.5E − 9 | 5.45E − 1 | 6.0E − 9 | 9.0E − 1 | 5.47E − 9 | 5.0E − 1 | 7.0E + 3 | 100 | 1.63E + 5 | 8.8E − 11 | 1.07E + 5 | 8.8E − 12 | 1.0E + 5 | 4.7E − 11 | 3.0E − 13 | 2.5E − 9 | 5.53E − 1 | 6.0E − 9 | 9.0E − 1 | 5.47E − 9 | 5.0E − 1 | 5.0E + 3 |
|
|