Abstract

Micro-nanocrystalline microstructures which are characterized by TiB2 platelets of the average thickness close to or smaller than 1 μm can be achieved in nearly full-density solidified TiC-TiB2 ceramic composites with Cr-based alloy phases by combustion synthesis in ultra-high gravity field of 2500 g. The filler phases in ceramic composites are actually Cr-based alloy with a little solidified solution of Ni atoms and Al atoms. The hardness, flexural strength, and fracture toughness of the materials are 18.5 ± 1.5 GPa, 650 ± 35 MPa, and 16.5 ± 1.5 MPa⋅m0.5, respectively. The improved fracture toughness of TiC-TiB2 ceramic composites results from crack deflection, crack bridging, and pull-out by a large number of fine TiB2 platelets and plastic deformation with some Cr-based alloy phases.

1. Introduction

TiC and TiB2 have become the promising candidates for cutting tools, wear-resistant parts, forming dies, and light-weight amour pieces, because of the many desirable properties they possess, such as high hardness, low density, high melting temperature, high corrosion resistance, good thermal shock resistance, and high temperature stability [1]. Meanwhile, the TiC-TiB2 composites exhibit excellent high-temperature performance which makes them also desirable for aircraft propulsion systems and thermal protection systems of space vehicle and nuclear fusion reactor. Therefore, in recent years many methods have been developed to prepare full-density TiC-TiB2 composites, such as high-pressure sintering (HPS) with or without sintering aids, reactive sintering (RS), reaction hot pressing (RHP), pressureless sintering (PS), spark plasma sintering (SPS), transient plastic phase processing (TPPP), self-propagating high-temperature synthesis (SHS), and combustion synthesis (CS) [25].

However, based on the achievements in preparing TiC-TiB2 composites, Vallauri et al. [2] concluded that the microstructures of bulk TiC-TiB2 composites were rarely characterized by the size of crystal grains close to or smaller than 1 μm, making the flexural strength of TiC-TiB2 composites hardly exceed 800 MPa [6]. Moreover, the known toughening mechanisms of the ceramics, such as transformation toughening and fiber toughening, are difficult to employ in TiC-TiB2 composites because of the extremely high sintering temperature which results in the fracture toughness of the materials generally smaller than 7.0 MPam0.5 [2]. Therefore, to promote the strengthening and toughening of hard materials, new approaches have always been sought and tried out to prepare bulk TiC-TiB2 composites with ultrafine-grained microstructures that possess intensive toughening mechanisms [7].

Combustion synthesis is being used to produce ceramics, intermetallics, and composite materials [8, 9]. Therefore, a new method, named combustion synthesis under high gravity, has been worked out to prepare high-hardness ceramic or cermets composites. This new approach has the advantages of high efficiency, low energy cost, simple equipment, and easy centrifugal forming [1013]. The paper will illustrate the experiment renewed by adjusting the components of the combustion system to control the composition of solidified TiC-TiB2 ceramic, which contributes to the ultrafine-grained microstructures of the materials. What is more, the paper will also expand on the microstructures and mechanical properties as well as the strengthening and toughening mechanisms of the solidified TiC-TiB2 ceramics with Cr-based alloy.

2. Experimental

Commercial powders of Ti (99.5% purity, <34 μm), B4C (97% purity, <3 μm), CrO3 (99.9% purity, <60 μm), Al (96% purity, <50 μm), and Ni (99.85% purity, <10 μm) were used as raw materials. The molar ratio (Ti to B4C) of 3 : 1 was chosen as the starting composition, so the composition of the solidified TiC-TiB2 composite was determined as TiC-66.7 mol % TiB2. According to previous research results [1416], due to the lower melting temperature and good wettability of Ni to TiC-TiB2, the introduction of Ni into combustion system could enhance the flowability and dwell time of ceramic liquid products, which will help to improve the density and homogeneity of ceramic products as a result of the forced convection and filling at the final stage of the solidification process. Based on the reason mentioned above, about 5 wt% Ni additive agent was introduced into the Ti + B4C combustion system, as shown in (1). In order to ensure high-temperature and full-liquid products after the combustion reaction, a 25 wt% (CrO3 + Al) subsystem was added as the activator to increase the combustion temperature, as shown in (2). Consider

The above powder blends were mechanically homogenized by ball milling for 1 h. After that, the graphite crucibles were filled with the reactive mixtures (1 kg) under uniaxially cold-press about 200 MPa. Then the graphite crucibles were inserted into the combustion chambers at the end of the rotating arms of the centrifugal machine. The combustion reaction was triggered by the electrical heat W wire (diameter of 0.5 mm) while the centrifugal machine provided a high-gravity acceleration of ( m/s2, where means the gravitational constant). When the combustion reaction was over, the centrifugal machine continued to run for 30 seconds. When the crucibles were cooled to ambient temperature, the ceramic discs of 150 mm in diameter and 15 mm in thickness were obtained after the samples were taken out of the graphite crucibles and the oxide slag at the top of the sample was eliminated by grinding.

The ceramic discs were cut and ground into rectangular bars measuring 3 mm (width) × 4 mm (height) × 36 mm (length) to determine their flexural strength. The flexural strength was measured by the three-point bending method with a cross-head speed of 0.5 mmmin−1 and a span of 30 mm. The indentation test was conducted with a loading time of 15 s and a load scale of 196 N to determine the hardness and fracture toughness of the ceramic composites. The phase composition was identified by X-ray diffraction (XRD; D/max-PA, Rigaku, Japan) with a step of 0.02° and a scanning rate of 2°/min. The microstructure and fracture morphology were examined by field emission scanning electron microscopy (FESEM; JSM-7001F, JEOL, Japan). The electron probe microanalysis (EPMA) was conducted by energy dispersive spectrometry (EDS).

3. Results and Discussion

The XRD spectra of the samples showed that the ceramics were mainly composed of the phases of TiC and TiB2. In addition, a few inclusions of α-Al2O3 and a minute amount of Cr-based alloy were also detected (as shown in Figure 1). The diffraction crystal planes of TiC were (111), (200), and (220), while the diffraction crystal planes of TiB2 were (001), (100), (101), and (002). The maximum diffraction-intensity crystal planes of TiC and TiB2 were (200) and (101), respectively. Because of the mole percent of Ni atoms which is much less than that of Cr atoms as well as the intersolubility of Cr and Ni at high temperature, the diffraction patterns of Cr but not Ni were detected by XRD in this experiment.

FESEM images and EDS spectra showed that a large number of randomly orientated, fine TiB2 platelets (presented by the dark areas in Figure 2) were uniformly embedded in irregular TiC grains (presented by the grey areas in Figure 2) and Cr-based alloy (presented by the white areas in Figure 2). Besides, a few inclusions of α-Al2O3 were also observed, as shown by the isolated black particles in Figure 2. For the white Cr-based alloy, some Ni atoms and residual Al atoms were detected by EDS results in Table 1, and the atomic ratio of Cr, Ni, Al was about 69 : 15 : 13. Consequently, it can be concluded that the alloy was actually the Cr-based alloy phase with a little solid solution of Ni atoms and residual Al atoms. CrO3 powder is a strong oxidant of the thermit, which is chemically unstable because of its decomposition at low temperature of 170°C [17]; the ignition of CrO3-Al mixture can occur at low temperature due to the presence of free oxygen atoms, as shown in (3). Judging from (2) and (3), the addition amount of Al powder to the combustion system is sufficient to support the thermit reaction, whereas the residual Al atoms have to be reserved in Cr-Ni liquid alloy, which in turn leads to the formation of the Cr-based alloy among the hard phases of TiC and TiB2 at the final stage of solidification, as shown in Figure 2:

The FESEM images showed that the refinement of TiB2 platelets was observed to arise from the centre to the surface of the sample, and the average thickness of TiB2 platelets decreased from about 2 μm at the center to 1 μm on the surface, whereas the average aspect ratio of TiB2 platelets changed from 5.25 to 2.38 inversely, as shown in Figures 2 and 3. White Cr-based alloy phases were rarely observed on the surface of the ceramic. Therefore, it can be concluded that the unique micro-nanocrystalline microstructure and the change in geometrical size of TiB2 platelets are closely dependent on the solidification behavior of the materials and the crystal growth of TiB2 and TiC.

Since the composition of the current TiC-TiB2 composites is chosen as TiC-66.7 mol% TiB2 of the hypereutectic composites based on some reports [18, 19], TiB2, in fact, acts as the primary phase to nucleate and precipitate from the melt. However, the TiC-TiB2 composite is achieved by rapid solidification, so crystal growth and crystal morphology of TiB2 are mainly controlled by the attachment energy of crystal plane to the atoms of Ti and B [20]. According to the atom-bonding strength of TiB2 lattice, that is, B–B > Ti–B > Ti–Ti, the growth velocities of crystal planes in TiB2 can be determined as () < () < () < () < () [21]. In other words, the crystallographic characteristics of TiB2 lattice lead to the anisotropy in crystal growth of TiB2, making TiB2 grow at the preferred crystal plane of high indices, such as () and (). Accordingly, as TiB2 crystal is in contact with TiC and other TiB2 crystals, or the high-indices planes of TiB2 crystal cannot capture enough Ti and B atoms to support its growth, the growth at high-indices planes of TiB2 crystal comes to a stop. However, the low-indices planes of TiB2 crystal continue to grow until the TiB2 crystal is enveloped by its low-indices crystal planes of () and (), and the TiB2 platelet with finite aspect ratio is developed while the low-indices crystal planes of (101) and (001) become the first-intensity and second-intensity diffraction planes of TiB2 phases, as illustrated in XRD spectra. Thereby, low-velocity faceting growth of TiB2 solid is one of the reasons for the achievement of fine TiB2 platelets and ultrafine-grained microstructures of the ceramic. With the continuous precipitation of TiB2 crystals out of the melt, TiC crystals also begin to precipitate as the concentration of C atoms in the melt becomes greater than the mole concentration of C which is indispensable to the nucleation of TiC crystal. Because TiC is characterized by a B1 (or NaCl-type) crystal structure with the isotropy in crystallography, it has a strong tendency of high-velocity nonfaceting growth. Therefore, under the dual influence of growth characteristics of TiC crystal and high diffusion rate of C relative to B [2], TiC grows much faster than TiB2 does once TiC is nucleated. Thus, the rapid growth of TiC not only contests against TiB2 for more Ti atoms, but also competes against TiB2 for more growing space, making it more difficult for TiB2 to be coarsened; then, a majority of TiB2 platelets are rapidly surrounded by irregular TiC grains. Therefore, the rapid growth of TiC second phase is another reason for the achievement of ultrafine-grained microstructures in current TiC-TiB2 composites.

In addition, crystal growth of TiB2 is also controlled by the solidification conditions, involving temperature gradient and heat dissipation of the melt. At the initial stage of solidification, high nucleation rate and low growth velocity of TiB2 crystals arise near the inner wall of the crucible due to high temperature gradient and fast heat dissipation. However, with the development of the heat-insulation ceramic solidifying toward the centre, heat dissipation and temperature gradient of the melt decrease while thermal diffusion in the melt increases inversely. Thus, the microstructure gradually transforms from nanocrystalline to microcrystalline, which can be illustrated by the increase in the average thickness of TiB2 platelets and the decrease in their average aspect ratio. The change in solidification behavior of the ceramic is also the reason for the concentration of Cr-Ni-Al alloy phases at the centre of the sample.

The relative density of TiC-TiB2 achieved measured 99.5%. The characteristics of combustion reaction in high-gravity field are similar to thermal explosives, which not only help the gas escape rapidly, but also form the thermal vacuum around liquid products. The achievement of the full-density ceramic derives both from the rapid solidification of the ceramic in high-gravity field and, more importantly, from the presence of Cr-Ni-Al alloy as the final solidified phase to eliminate shrinkage cavities. The hardness, flexural strength, and fracture toughness of the current solidified TiC-TiB2 measured  GPa,  MPa, and  MPam0.5. Compared with the maximum hardness of 28.5 GPa [14], the maximum flexural strength of  MPa [14], and the maximum fracture toughness of  MPam0.5 [22] reported by the literature, the current TiC-TiB2 composite has higher fracture toughness, yet, its hardness is only moderate. It is worthy to note that despite the general moderate hardness measured in current composites, the maximum hardness of 20.0 2.0 GPa was achieved on the surface, while the minimum hardness of  GPa was achieved in the center of the ceramic. Therefore, the presence of Cr-Ni-Al alloy phases is the very reason for the average hardness of the current composite, smaller than one of the materials prepared by early experiments.

FESEM fracture morphologies showed that the fracture behavior of TiC-TiB2 composite ceramics presented a mixed mode of transgranular fracture in TiC irregular grains and intercrystalline fracture along TiB2 platelets, and the grooves of TiB2 platelets clearly remained at fracture section of the ceramic after they were peeled out of the ceramic matrix, as shown in Figure 4. Meanwhile, FESEM images of crack propagation paths showed that crack deflection and crack bridging seemed to be the main interaction mechanisms of the crack and TiB2 platelets, as shown in Figure 5.

According to the literature [23], the larger grain size of TiC crystals means the smaller critical shear stress inducing the cracking of TiC grains, so transcrystalline fracture almost takes place in the coarsened irregular TiC grains as shown in Figure 6(a). At ambient temperature, the cleavage surface and tearing ridge, which were taken as typical brittle transcrystalline fracture features, can be partially seen on fracture surfaces as shown in Figure 6(b). It is also demonstrated that TiC phases have little effect on ceramic toughening, but they do play a role in ceramic strengthening by refining the microstructure of the ceramic during solidification. As for TiB2, in contrast, the crack is firstly arrested and crack-pinning effect is initiated as the crack is met by these small-thickness TiB2 platelets, which results from their high elastic modulus, high volume fraction, plate-like morphology, and highly random distribution, especially their thickness close to or smaller than 1 μm. Subsequently, the crack has to propagate around the TiB2 platelets due to the weak interfacial bonding between TiB2 phases and the other ones, and crack deflection toughening mechanism occurs. With the propagation of the crack and the debonding at the interfaces of TiB2 platelets, secondary microcracks develop along the boundaries of TiB2 phases, resulting in the presence of crack bridging along with frictional interlocking as a result of the growth of secondary microcracks at both sides of the interface. Finally, crack bridging or pull-out of TiB2 platelet is accomplished, as shown in Figure 7. Thus, greater crack-opening displacement within the bridging zone is achieved, whereas the stress concentration around the crack tip is relieved due to the presence of the closure stress behind it, which in turn results in greater resistance to crack propagation in the ceramic. Therefore, it is reasonable to conclude that, by acting as the reinforcement in the ceramic, small-thickness TiB2 platelets play a predominant role in strengthening and toughening the ceramic through their interaction with the crack to induce the toughening mechanisms of crack deflection, crack bridging, or pull-out of the platelet. In addition, the fracture toughness on the surface of the ceramic measures  MPam0.5 by indentation test, whereas the fracture toughness in the central part measures  MPam0.5. Slight yield phenomenon can also be observed in load-displacement curve of the material, so we can come to the conclusion that, besides the toughening mechanisms induced by TiB2 platelets, Cr-Ni-Al alloy phases also play an important role in toughening ceramic through their plastic deformation, as shown in Figure 8. When the crack extends through the Cr-Ni-Al alloy phases and forms the cleavage steps and tear ridges, the transgranular cleavage fracture is more easily to arise in the Cr-based alloy phases with some aluminum and nickel content, as shown in Figure 9.

Accordingly, by combining the microstructures of the ceramic with linear elastic fracture mechanics for I-mode crack [24], high flexural strength of the current composite is considered to derive from the achievement of full-density ceramic, high volume fraction of high-elastic-modulus TiB2. Moreover, the achievement of micro-nanocrystalline microstructure in the full-density ceramic secures high fracture toughness, and the fracture behavior of the ceramic composites is controlled by the intensively coupled mechanisms of crack deflection, crack bridging, or pull-out by a large number of fine TiB2 platelets, along with the plastic deformation of the Cr-Ni-Al alloy phases.

4. Conclusion

To sum up, TiC-TiB2 ceramic composites with micro-nanocrystalline microstructures can be achieved by combustion synthesis in high-gravity field. XRD, FESEM, and EDS show that a large number of fine TiB2 platelets are uniformly embedded in irregular TiC grains, and a few Cr-Ni-Al alloy phases can be detected in or between those phases. The average thickness of TiB2 platelets decreases from the center to the surface of the materials, whereas their average aspect ratio increases inversely. Cr-Ni-Al alloy phases are also found in the central part of the composite. The achievement of micro-nanocrystalline microstructures, characterized by TiB2 platelets with the average thickness close to or smaller than 1 μm in the ceramic, results from the low-velocity faceting growth of TiB2 crystal due to its anisotropy in crystallography, the high-velocity nonfaceting growth of TiC solid due to its isotropy in crystallography, and high diffusion rate of B relative to C in liquid TiC-TiB2. These combine to make the growth velocity of TiC faster than that of TiB2, despite the fact that the TiB2 solid serves as the leading phase at the initial stage of solidification, which hardly renders TiB2 platelets to grow and coarsen so as to be surrounded rapidly by irregular TiC grains during solidification. The relative density of TiC-TiB2 composites measures 99.5%, and the achievement of the nearly full-density composites is a result of the rapid solidification of the ceramics in high-gravity field and the presence of a few low-melting-point Cr-based alloys. The hardness, flexural strength, and fracture toughness of solidified TiC-TiB2 measure  GPa,  MPa, and  MPam0.5, respectively. High flexural strength of the materials is achieved as a result of the high volume fraction of high-elastic-modulus TiB2. The high fracture toughness derives from intensively coupled mechanisms of crack deflection, crack bridging, and pull-out by a large number of fine TiB2 platelets as well as the plastic formation of Cr-Ni-Al alloy phases.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

This work is sponsored by National Natural Science Foundation of China (Grant no. 51072229).